Abstract:The influences of surface conditions, including surface roughness and oxidation state, on the total hemispherical emissivity were experimentally investigated using an improved steady-state calorimetric technique for iron-based alloy samples. The investigated samples were prepared using rough polishing grits and high-temperature oxidization. The surface micrograph, roughness and composition of the oxide layer were analyzed using scanning electron microscope (SEM) and auger electron spectroscope (AES) to quantitatively describe the surface characteristics. Results of two iron-based alloy samples with different surface roughnesses showed that the measured total hemispherical emissivity increased with the roughness. However, the effect of surface roughness on total hemispherical emissivity gradually became smaller at high temperatures above 1200. K for the investigated roughness conditions of iron-based alloys. Another six iron-based alloy samples were pre-oxidized in a high-temperature air muffle furnace with three oxidized at 400. °C and the other three oxidized at 600. °C for various times. The results showed that the emissivities of samples oxidized at 400. °C for various times were similar to each other and the un-oxidized substrate, while the emissivities of samples oxidized at 600. °C increased with oxidation time. This distinction arose from the different oxide layer thickness as the oxidation time increased at 600. °C, while the thickness was almost constant at 400. °C. The characteristics of the oxide layer grown in different oxidation temperatures were different as well. For the same oxidation time, the emissivities of samples oxidized at the higher oxidation temperature were larger than the values of samples oxidized at lower oxidation temperature. At high temperature (600. °C) oxidation process of iron-based alloys, the oxide layer might be compact and its density was large which would strength the capacity of radiation heat transfer of iron-based alloy, comparing with the oxide layer grown in low temperature (400. °C) oxidation process at the same oxidation time. © 2012 Elsevier Inc.

Studies on the Emittance of Stainless Steel Surface

Spectral emittance measurements of micro/nanostructures in energy conversion: a review

Surface Characterization of Stainless Steels Prepared with Various Surface Treatments

Parameters optimization of electrolytic plasma polishing of austenitic stainless steel and surface performance analysis

An X-ray photo-electron spectroscopic study of surface treatments of stainless steels

Prediction of the normal spectral emissivity of metals with different surface roughness using a modified ray-tracing method

Experimental Measurement of Emissivity of Polished Steel Strips from a Continuous Annealing Line

Investigation on the Dry-Type Electrochemical Polishing of 304 Stainless Steel with Ion-Exchange Resin Particles

Low current density electropolishing and corrosion resistance study of 304 stainless steel

Investigating the Surface Tension of Steels using Electromagnetic Levitation, Part I: Iron-Nickel Alloys

Two-Steps Electrochemical Polishing of Laser Powder Bed Fusion 316L Stainless Steel

Chemical States of Stainless Steel in nm to Several Tens of nm Region from Surface Observed by the Depth-Resolved X-ray Absorption Spectroscopy

Research on the surface characteristics of 42CrMo alloy steel pulse electrochemical machining

Errosion-Corrosion Critical Performance of Surface Nanocrystalline 20 Carbon Steel in Condensate Water

Study on Dry-Ice Particle Jet Polishing Process of 316L Stainless Steel Electrode

Analytical Study on Emittance Growth Caused by Roughness of A Metallic Photocathode

Electropolishing study of metastable austenitic steel AISI 347 for EBSD analyses

Electrochemical Polishing of Austenitic Stainless Steels

Experimental research on the influence of surface conditions on the total hemispherical emissivity of iron-based alloys

Chemical Mechanical Polishing of Stainless Steel As Solar Cell Substrate

Electrochemical polishing versus mechanical polishing of AISI 304: surface and electrochemical study