Phase-field simulation on the hétéroépitaxial nucléation of (Fe,Co) solid solution on facet phase in undercooled liquid
Wenjing Yao,Zipeng Ye,Nan Wang,Jehyun Lee
DOI: https://doi.org/10.1016/j.jallcom.2013.06.188
IF: 6.2
2013-01-01
Journal of Alloys and Compounds
Abstract:The nucleation process of (Fe,Co) solid solution epitaxially grown on the primary phase (Si) has been investigated by the phase-field method in Fe-41 wt%Co alloy. The effects on nucleation by such factors as the crystal orientation of the primary phase, the undercooling, the interface thickness, the anisotropy factor, the effective deposition rate, and the phase-field variable of primary phase were analyzed in great details. The results show that the nucleus morphology on Si {111} crystal surface is more complete than those on Si{110} and Si {100}. At high undercooling, more defects form in the nucleus. When the ratio of the interface thickness to the capillary length is W-0/d(0) = 5, the nucleus contain the least defects. As the anisotropy coefficient increases, the interface disturbance of the nucleus is more complex. But when the anisotropy coefficient is epsilon = 0.03, the interface disturbance is the minimal, and the nucleus morphology is the most integrated. The nucleation radius increases as the effective deposition rate rises from 2 to 7 ML/s. When the phase-field variable of primary phase takes phi(s) = 0, the nucleus morphology is the most complete. (C) 2013 Elsevier B.V. All rights reserved.