Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Sonochemical Fabrication of Mesoporous TiO2 Inside Diatom Frustules for Photocatalyst

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Synthesis of Nano-Tio2/diatomite Composite and Its Photocatalytic Degradation of Gaseous Formaldehyde

Hydrothermal Synthesis and Morphological Evolution of Mesoporous Titania−Silica

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Preparation and photocatalytic performance of TiO_2-mounted diatomite composites by a hydrothermal method

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Sonochemical incorporation of nanosized TiO2 inside mesoporous silica with high photocatalytic performance

Sonochemical fabrication of morpho-genetic TiO 2 with hierarchical structures for photocatalyst

Mesoporous TiO2 Single-Crystal Particles from Controlled Crystallization-Driven Mono-Micelle Assembly As an Efficient Photocatalyst.

Three-dimensional Interconnected Mesoporous Anatase TiO2 Exhibiting Unique Photocatalytic Performances

Macro-Sized Hierarchical Nanostructured TiO 2 /titanosilicate Composite with Enhanced Photocatalytic Activity

Controllable Synthesis of Mesoporous F–TiO2 Spheres for Effective Photocatalysis

Mesoporous Tio2 Micro-Nanometer Composite Structure: Synthesis, Optoelectric Properties, and Photocatalytic Selectivity

Sonochemical Synthesis and Photocatalytic Activity of Meso- and Macro-Porous TiO(2) for Oxidation of Toluene.

Synthesis of Uniform Ordered Mesoporous TiO2 Microspheres with Controllable Phase Junctions for Efficient Solar Water Splitting

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution

In Situ Synthesis of the Mesoporous C–TiO2 Microspheres Derived from Partial Hydrolysis Tetrabutyl Titanate for Enhanced Photocatalytic Degradation under Visible Light

Mesoporous hollow sphere titanium dioxide photocatalysts through hydrothermal silica etching

Preparation and Characterization of Mesoporous SBA-15 Supported Dye-Sensitized TiO2 Photocatalyst