H-Bonding Supramolecular Hydrogels with Promising Mechanical Strength and Shape Memory Properties for Postoperative Antiadhesion Application
Yuxuan Yang,Xiaodan Zhao,Jing Yu,Xiaojing Chen,Xingxing Chen,Chenhui Cui,Junjie Zhang,Qiang Zhang,Yanfeng Zhang,Shuang Wang,Yilong Cheng
DOI: https://doi.org/10.1021/acsami.0c07753
2020-07-07
Abstract:Development of a physical barrier with mechanical properties similar to human smooth muscle and an on-demand degradation profile is crucial for the clinical prevention of postoperative adhesion. Herein, a series of supramolecular hydrogels (PMI hydrogels) composed of poly(ethylene glycol) (PEG), methylenediphenyl 4, 4-diisocyanate (MDI), and imidazolidinyl urea (IU, hydrogen bonding reinforced factor) with biodegradability and high toughness are reported to serve as physical barriers for abdominal adhesion prevention. The tensile fracture strength and strain of the PMI hydrogels could be adjusted in the ranges of 0.6–2.3 MPa and 100–440%, respectively, and their Young's moduli (0.2–1.6 MPa) are close to that of human soft tissues like smooth muscle and skin tissue as well as they have outstanding shape memory properties. The PMI hydrogels show good cell and tissue biocompatibility, and the in vivo retention time is in accord with the needs for the postoperative antiadhesion physical barriers. Through an abdominal defect model on mice, this study shows that the PMI hydrogel can completely prevent tissue adhesion compared to the commercialized Seprafilm with high safety. Owing to the promising mechanical properties and good biocompatibility, the PMI hydrogels may be extended for various biomedical applications and the development of advanced flexible electronic devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c07753?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c07753</a>.Details of the experimental methods, supplementary characterization data (<sup>1</sup>H NMR, photographs of hydrogels swollen in water and urea solution, SEM, consecutive loading–unloading cyclic tests, self-recovery capability, recovery efficiency, shape-fixing ratio and shape-recovery ratio of PMI-1 hydrogel, cell viability, in vivo degradation, H&E staining of the normal tissue, photographs of the surgery process and wound recovery, and the subtypes of the cells and fibrous tissue in the antiadhesion test) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c07753/suppl_file/am0c07753_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology