Abstract:Microencapsulated ammonium polyphosphate (GMAAPP) and microencapsulated expanded graphite (PUEG) were prepared by in situ polymerization with glycidyl methacrylate (GMA) and polyurethane as the shell material respectively. Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and thermogravimetry (TG) were used to characterize GMAAPP and PUEG. The results confirmed the successful fabrication of GMAAPP and PUEG. On this basis, a series of flame-retardant rigid polyurethane foam composites were prepared with GMAAPP and PUEG loading by the one-step water-blown method. The flame retardancy, mechanical properties, thermal insulation, and thermal stability of RPUF/GMAAPP30, RPUF/PUEG30, and RPUF/GMAAPP20/PUEG10 composites were investigated by limiting oxygen index (LOI), Underwriters Laboratories vertical burning test (UL-94), TG, thermal conduction and density test. The results showed that the thermal stability at the high temperature of RPUF composites can be improved by the addition of GMAAPP and PUEG. SEM test confirmed significantly enhanced compatibility between the microencapsulated flame retardant particles and RPUF matrix, which obviously improved the integrity of the cell structure. RPUF/GMAAPP30, RPUF/PUEG30 and RPUF/GMAAPP20/PUEG10 exhibited LOI of 22.3 vol%, 25.3 vol%, 24.6 vol% with all composites passed V-0 rating in UL-94 test. The physical performance test indicated that RPUF/GMAAPP20/PUEG10 exhibited thermal conductivity of 0.0395 W/m·K and compressive strength of 0.292 MPa, which possessed the best comprehensive physical performance. Char residue analysis suggested the combination of GMAAPP and PUEG increased graphitization degree and compactness of char residues for RPUF composites, thus effectively improving the fire safety of the composite.Graphical

Effects of Inorganic Fillers on the Flame‐retardant and Mechanical Properties of Rigid Polyurethane Foams

Structure and Flame-Retardant Actions of Rigid Polyurethane Foams with Expandable Graphite.

Flame retardancy of hollow glass microsphere/rigid polyurethane foams in the presence of expandable graphite

Effects Of Expandable Graphite And Ammonium Polyphosphate On The Flame-Retardant And Mechanical Properties Of Rigid Polyurethane Foams

Flame‐retardant and Mechanical Properties of Rigid Polyurethane Foam/mrp/mg(oh)2/gf/hgb Composites

Influence of Expandable Graphite on Comprehensive Performance of All-Water Blown Flame Retardant Rigid Polyurethane Foams

Understanding the Flame Retardant Mechanism of Intumescent Flame Retardant on Improving the Fire Safety of Rigid Polyurethane Foam

Dependence of flame-retardant properties on density of expandable graphite filled rigid polyurethane foam

Flame‐retardant and Mechanical Properties of High‐density Rigid Polyurethane Foams Filled with Decabrominated Dipheny Ethane and Expandable Graphite

Synthesis and characterization of expandable graphite–poly(methyl methacrylate) composite particles and their application to flame retardation of rigid polyurethane foams

Rigid Polyurethane Foam Compounds with Excellent Fire Performance Modified by a Piperazine Pyrophosphate/expandable Graphite Synergistic System

Synthesis, physical-mechanical properties and fire behaviors of polyurethane foam with reactive flame retardant and expandable graphite

Expandable Graphite‐methyl Methacrylate‐acrylic Acid Copolymer Composite Particles As a Flame Retardant of Rigid Polyurethane Foam

Flame retardancy of different-sized expandable graphite particles for high-density rigid polyurethane foams

Effect of Compound Halogen-Free Flame Retardants on Flame Retardant Properties of Rigid Polyurethane Foam

Synergistic Effect Of Expandable Graphite And Aluminum Hypophosphite On Flame-Retardant Properties Of Rigid Polyurethane Foam

Aluminum Hypophosphite in Combination with Expandable Graphite As A Novel Flame Retardant System for Rigid Polyurethane Foams

Inorganic/organic Phosphorus‐based Flame Retardants Synergistic Flame Retardant Rigid Polyurethane Foam

Synergistic effect of expandable graphite and phenylphosphonic-aniline salt on flame retardancy of rigid polyurethane foam

Flame retardant rigid polyurethane foam composites based on microencapsulated ammonium polyphosphate and microencapsulated expanded graphite

Highly Efficient Flame Retardancy and Fire Spread Behavior of Rigid Polyurethane Foams with extremely low content of Flame Retardant