Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Hot Ductility Of Eco-Friendly Low Carbon Resulphurised Free Cutting Steel With Bismuth

EFFECTS OF B ON HIGH TEMPERATURE MECHA-NICAL PROPERTIES AND THERMAL FATIGUE BEHAVIOR OF COPPER DIE-CASTING DIE STEEL

The Effect of Bismuth on Technological and Material Characteristics of Low-Alloyed Automotive Steels with a Good Machinability

Effect of B2 Precipitation on Hot Ductility of Fe–22Mn–9Al–0.6C Low-Density Steel

Hot Ductility Prediction Model of Cast Steel with Low-Temperature Transformed Structure during Continuous Casting

Effect of Sulfur on Antimony-Induced High-Temperature Ductility Deterioration of C-Mn Steel

Hot Ductility Behavior of Boron Containing Microalloyed Steels with Varying Manganese Contents

Thermal Deformation Behavior of Bismuth-Containing Stainless Steel

Effect of Bismuth and Telluride on the Inclusions of Sulfur Free-Cutting Steel

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Hot ductility behavior of medium carbon sulfur-containing alloy steel

Relation between the Metallographic Structure and Mechanical Properties of a Bimetallic Steel Bar after Fire

Effect of Boron on Hot Ductility and Room-Temperature Tensile Properties of Microalloyed Steels with Titanium and Niobium

Microstructure and mechanical properties of a low-carbon HDQ&P steel

Microstructure and Properties of Low and Medium Carbon of High-boron Cast Steel

Hot Ductility of High Carbon Steel Produced by Csp

Influence of Ti and V on the Hot Ductility of High Manganese Austenitic Steel

Effect of Bismuth Content and Heating Rate on MnS Inclusions in Free-Cutting Steel

Effect of Heat Treatment on Structure and Properties of B Alloyed High Speed Steel for Rolling Mill Rolls

A Study of Heat Treatment of High‐boron High‐speed Steel Roll

The Influence of Thermomechanical Conditions on the Hot Ductility of Continuously Cast Microalloyed Steels