Abstract:Bone-like biological materials have achieved superior mechanical properties through hierarchical composite structures of mineral and protein. Geckos, and many insects have evolved hierarchical surface structures to achieve superior adhesion capabilities. What is the underlying principle of achieving superior mechanical properties of materials? Using joint atomistic-continuum modeling, we show that the nanometer scale plays a key role in allowing these biological systems to achieve such properties, and suggest that the principle of flaw tolerance and design for robustness may have had an overarching influence on the evolution of the bulk nanostructure of bone-like materials and the surface nanostructure of gecko-like animal species. We illustrate that if the characteristic dimension of materials is below a critical length scale on the order of several nanometers, Griffith theory of fracture no longer holds. An important consequence of this finding is that materials with such nano-substructures become flaw-tolerant, as the stress concentration at crack tips disappears and failure always occurs at the theoretical strength of materials, regardless of defects. The atomistic simulations complement continuum analysis and reveal a smooth transition between Griffith modes of failure via crack propagation to uniform bond rupture at theoretical strength below a nanometer critical length. This modeling resolves a long-standing paradox of fracture theories, and these results have important consequences for understanding failure of small-scale materials. Additional investigations focus on shape optimization of adhesion systems. We illustrate that optimal adhesion can be achieved when the surface of contact elements assumes an optimal shape. The results suggest that optimal adhesion can be achieved either by length scale reduction, or by optimization of the contact shape. Whereas change in shape does not lead to robustness, reducing the dimension results in robust adhesion devices.

On Flaw Tolerance of Nacre: a Theoretical Study.

Damage-Tolerance Strategies for Nacre Tablets

Nanostructured individual nacre tablet: a subtle designed organic–inorganic composite

Cracks Fail to Intensify Stress in Nacreous Composites

Discontinuous crack-bridging model for fracture toughness analysis of nacre

The weak interfaces within tough natural composites: experiments on three types of nacre

Nacre-mimetic Composite with Intrinsic Self-Healing and Shape-Programming Capability

Fabrication and Characterisation of Alumina/aluminium Composite Materials with a Nacre-Like Micro-Layered Architecture

Nacre's Brick–mortar Structure Suppresses the Adverse Effect of Microstructural Randomness

Printing nature: Unraveling the role of nacre's mineral bridges

Failure progression and toughening mechanism of 3D-printed nacre-like structures under in-plane compression

Biomimetic Research Based on the Study of Nacre Structure

Flaw Tolerant Nanostructures of Biological Materials

Flaw Tolerance in a Viscoelastic Strip

Materials Become Insensitive to Flaws at Nanoscale: Lessons from Nature

Crystal Orientation, Toughening Mechanisms and a Mimic of Nacre

Atomistic and Continuum Studies of Flaw Tolerant Nanostructuresin Biological Systems

Artificial Nacre with High Toughness Amplification Factor: Residual Stress‐Engineering Sparks Enhanced Extrinsic Toughening Mechanisms

Atomistic And Continuum Studies Of Flaw Tolerant Nanostructures In Biological Systems

Fracture behaviors of nacre-like composites via phase-field fracture modeling

Interfacial Strength-Controlled Energy Dissipation Mechanism and Optimization in Impact-Resistant Nacreous Structure