Abstract:Fe 3 O 4 /PVP//Eu(BA) 3 phen/PVP magnetic-photoluminescent bifunctional bistrand-aligned composite nanofibers bundles based on ferroferric oxide(Fe 3 O 4 ) nanoparticles and europium complex Eu(BA) 3 phen (BA = benzoic acid) were fabricated via electrospinning by employing a homemade parallel axial electrospinning setup with the side by side dual spinnerets for the first time. The structures, morphology, and properties of the as-prepared products were investigated in detail by X-ray diffraction, field-emission scanning electron microscopy, energy dispersive spectroscopy, transmission electron microscopy (TEM), a fluorescence spectrometer, and a vibrating sample magnetometer. SEM analysis showed the average diameter of the individual-strand fiber of the bistrand-aligned composite nanofibers bundles was 200 ± 25 nm. TEM image demonstrated that Fe 3 O 4 nanoparticles were only dispersed into one strand of the bistrand-aligned composite nanofibers bundles, and the average diameter of Fe 3 O 4 nanoparticles was about 15 nm. Under the excitation of 274 nm ultraviolet light, Fe 3 O 4 /PVP//Eu(BA) 3 phen/PVP bistrand-aligned composite nanofibers bundles exhibited red emissions of predominant peaks at 592 and 616 nm, which were respectively attributed to the 5 D 0 → 7 F 1 and 5 D 0 → 7 F 2 transitions of Eu 3+ ions. The fluorescence intensity of the bistrand-aligned composite nanofibers bundles was higher than that of Fe 3 O 4 /Eu(BA) 3 phen/PVP composite nanofibers, and was decreased with the increase of the amounts of Fe 3 O 4 nanoparticles. The saturation magnetizations of the bistrand-aligned composite nanofibers bundles and the Fe 3 O 4 /Eu(BA) 3 phen/PVP composite nanofibers were about equal when the two nanostructures contained the same mass ratios of Fe 3 O 4 nanoparticles, but the saturation magnetizations of the bistrand-aligned composite nanofibers bundles were increased with the increase of the amounts of Fe 3 O 4 nanoparticles. The new type Fe 3 O 4 /PVP//Eu(BA) 3 phen/PVP bistrand-aligned composite nanofibers bundles have potential applications in many fields due to their superparamagnetism behavior and high fluorescence intensity. Meanwhile, the research results will provide a new method for the preparation of the other two components of polymer fibers.

Electrospinning Fabrication and Characterization of Magnetic-Upconversion Fluorescent Bifunctional Core–shell Nanofibers

Electrospinning Preparation and Properties of Magnetic-Photoluminescent Bifunctional Coaxial Nanofibers

Electrospinning Fabrication of High-Performance Magnetic@photoluminescent Bifunctional Coaxial Nanocables

Magnetic-Upconversion Luminescent Bifunctional Flexible Coaxial Nanoribbon and Janus Nanoribbon: One-Pot Electrospinning Preparation, Structure and Enhanced Upconversion Luminescent Characteristics

Flexible Janus Nanofiber to Help Achieve Simultaneous Enhanced Magnetism-Upconversion Luminescence Bifunction

Fabrication of Magnetic-Luminescent Bifunctional Composite Nanofibers Via Facile Electrospinning

One-pot Coaxial Electrospinning Fabrication and Properties of Magnetic-Luminescent Bifunctional Flexible Hollow Nanofibers

Fabrication of Magnetic-Fluorescent Bifunctional Flexible Coaxial Nanobelts by Electrospinning Using a Modified Coaxial Spinneret.

Electrospinning preparation and properties of magnetic-photoluminescent bifunctional bistrand-aligned composite nanofibers bundles

Electrospinning fabrication and properties of Fe3O 4/Eu(BA)3phen/PMMA magnetic-photoluminescent bifunctional composite nanoribbons

Coaxial Electrospinning Preparation and Properties of Magnetic–photoluminescent Bifunctional CoFe 2 O 4 @Y 2 O 3 :Eu 3+ Coaxial Nanofibers

Janus Nanofiber: A New Strategy to Achieve Simultaneous Enhanced Magnetic-Photoluminescent Bifunction

Conjugate Electrospinning-Fabricated Nanofiber Yarns Simultaneously Endowed with Bifunctionality of Magnetism and Enhanced Fluorescence

A New Strategy to Assemble Enhanced Magnetic–photoluminescent Bifunction into a Flexible Nanofiber

Water-soluble Luminescent‐electrical‐magnetic Trifunctional Composite Nanofibers Prepared Via Electrospinning Technique

Electrospinning preparation and properties of Fe 3 O 4 /Eu(BA) 3 phen/PVP magnetic-photoluminescent bifunctional composite nanofibers

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Coaxial Nanofibers to Help Achieve Tunable and Enhanced Simultaneous Magnetic-Luminescent Bifunctionality

Tunable and enhanced simultaneous magnetism-luminescence bifunctionality assembled into a coaxial nanofiber

Facile electrospinning construction and characteristics of coaxial nanobelts with simultaneously tunable magnetism and color-tuned photoluminescence bifunctionality

Tuned magnetism–luminescence bifunctionality simultaneously assembled into flexible Janus nanofiber