Abstract:To achieve rapid, efficient, and low-cost preparation of large-scale stable aluminum alloy superhydrophobic surfaces, a new preparation method is proposed. The outer surface of the array micro-protrusions was coated with a layer of armor, which was the molten spatter produced during picosecond laser processing. The molten sputters and micro-protrusions combined to form micro–nano composite multi-layer structures. Through these special array micro–nano composite multi-layer structures and chemical modification, the wear-resistant and superhydrophobic properties of aluminum alloy surfaces were realized. According to test results, the array micro–nano composite structures prepared by picosecond laser and chemical modification had a water drop contact angle of 154.6° and a water drop rolling angle of 2°, exhibiting excellent superhydrophobic and anti-adhesion properties. Its self-cleaning, corrosion resistance and friction and wear behavior were systematically analyzed. The analysis results showed that the rolling droplets on the prepared surface could easily take away contaminants. The corrosion voltage and corrosion current density of the prepared superhydrophobic surface are significantly lower than that of the raw surface. In addition, a water drop contact angle of the aluminum alloy sample maintained at 145.1° after five wear tests, indicating the prepared surface after wear testing still had hydrophobic performance. The innovative method proposed in this study provides a simple and effective method for preparing large-scale wear-resistant superhydrophobic surface of aluminum alloy.

Fabrication of Biomimetic Super-Hydrophobic Surface on Aluminum Alloy

Fabrication of Superhydrophobic Surface with Different Metal Films on Aluminum Alloy

Controllable Construction and Corrosion Resistance Mechanism of Durable Superhydrophobic Micro-Nano Structure on Aluminum Alloy Surface

Fabrication of wear-resistant and superhydrophobic aluminum alloy surface by laser-chemical hybrid methods

Robust and Chemically Stable Superhydrophobic Aluminum-Alloy Surface with Enhanced Corrosion-Resistance Properties

Fabrication of biomimetic anisotropic super-hydrophobic surface with rice leaf-like structures by femtosecond laser

Fabrication of Superhydrophobic Surface on Anodized Aluminum Through a Wet-Chemical Route

Synthesis of Biomimetic Superhydrophobic Surface Through Electrochemical Deposition on Porous Alumina

Fabrication of superhydrophobic aluminum alloy surfaces by nickel and phosphorus chemical deposition

Anti-corrosion superhydrophobic surfaces of Al alloy based on micro-protrusion array structure fabricated by laser direct writing

Fabrication of anodized superhydrophobic 5083 aluminum alloy surface for marine anti-corrosion and anti-biofouling

A simple fabrication method for mechanically robust superhydrophobic surface by hierarchical aluminum hydroxide structures

Fabrication of a Highly Stable Superhydrophobic Surface with Dual-Scale Structure and Its Antifrosting Properties

Robust superhydrophobic surface on Al substrate with durability, corrosion resistance and ice-phobicity

Aluminum Alloy Super-Hydrophobic Surface Fabrication Via Electrochemical Etching Method

Fabrication of Superhydrophobic AA5052 Aluminum Alloy Surface with Improved Corrosion Resistance and Self Cleaning Property

Fabrication of Super-Hydrophobic Surfaces on Aluminum Alloy Substrates by RF-sputtered Polytetrafluoroethylene Coatings

Fabrication of biomimetic superhydrophobic and anti-icing Ti6Al4V alloy surfaces by direct laser interference lithography and hydrothermal treatment

Superhydrophobic Self-Assembled Silane Monolayers on Hierarchical 6082 Aluminum Alloy for Anti-Corrosion Applications

Facile fabrication of a robust and corrosion resistant superhydrophobic aluminum alloy surface by a novel method