Effect of Trace B on the Microstructure and Mechanical Properties of a Newly Near α High Temperature Titanium Alloy
Chongxiao Guo,Changjiang Zhang,Jianchao Han,Shuzhi Zhang,Fei Yang,Lihua Chai,Ziyong Chen
DOI: https://doi.org/10.1002/adem.201700490
IF: 3.6
2017-08-08
Advanced Engineering Materials
Abstract:In this study, the microstructural evolution and mechanical properties of a newly near α titanium alloy with trace additions of B by in situ casting route are investigated. The results show that the coarse prior β grain and α lath within matrix alloy are gradually refined with increasing of B addition. The relative refinement mechanism of prior β grain and α lath width is analyzed and discussed. In addition, it is shown that both of ultimate compressive strength (UCS) and yield strength (UYS) increase with B addition, which is mainly attributed to microstructural refinement. However, the compressive ductility and fracture toughness decrease with increasing of B addition, which is due to the cracking of TiB, leading to the acceleration of crack extension. A newly near α titanium alloy with trace addition of B are discussed. Necklace‐like of TiB locates at the grain boundary of prior β–Ti. According to the solidification path of B‐containing alloys, refinement mechanism is elaborated. Ultimate compressive strength and yield strength increase, while the compressive ductility and fracture toughness decrease with B addition.
materials science, multidisciplinary