Zn and N Codoped TiO 2 Thin Films: Photocatalytic and Bactericidal Activity
Abdullah M. Alotaibi,Premrudee Promdet,Gi Byoung Hwang,Jianwei Li,Sean P. Nair,Sanjayan Sathasivam,Andreas Kafizas,Claire J. Carmalt,Ivan P. Parkin
DOI: https://doi.org/10.1021/acsami.1c00304
2021-02-17
Abstract:We explore a series of Zn and N codoped TiO<sub>2</sub> thin films grown using chemical vapor deposition. Films were prepared with various concentrations of Zn (0.4–2.9 at. % Zn vs Ti), and their impact on superoxide formation, photocatalytic activity, and bactericidal properties were determined. Superoxide (O<sub>2</sub><sup>•–</sup>) formation was assessed using a 2,3-bis(2-methoxy-4-nitro-5-sulfophenyl)-5-[(phenylamino)carbonyl]-2<i>H</i>-tetrazolium sodium salt (XTT) as an indicator, photocatalytic activity was determined from the degradation of stearic acid under UVA light, and bactericidal activity was assessed using a Gram-negative bacterium <i>E. coli</i> under both UVA and fluorescent light (similar to what is found in a clinical environment). The 0.4% Zn,N:TiO<sub>2</sub> thin film demonstrated the highest formal quantum efficiency in degrading stearic acid (3.3 × 10<sup>–5</sup> molecules·photon<sup>–1</sup>), while the 1.0% Zn,N:TiO<sub>2</sub> film showed the highest bactericidal activity under both UVA and fluorescent light conditions (>3 log kill). The enhanced efficiency of the films was correlated with increased charge carrier lifetime, supported by transient absorption spectroscopy (TAS) measurements.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c00304?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c00304</a>.EDS results (Table S1), structural change of XTT to XTT formazan schematic (Figure S1), UV–vis spectra of XTT on Zn, N doped TiO<sub>2</sub> films under UVA irradiation (Figure S2), and TAS decay results (Figures S3–S6) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c00304/suppl_file/am1c00304_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology