Abstract:Polyelectrolyte multilayer films were fabricated by layer-by-layer deposition of polyacrylic acid (PAA) and polyethyleneimine (PEI). The (PAA/PEI) films showed unique dynamic properties owning to the high mobility of the polymer molecules: the spongy microporous structure was formed through an acid treatment for 60 min; and the porous structure disappeared under a 100% relative humidity treatment, back to a solid film Based on this (PAA/PEI) platform, lysozyme was easily loaded into the film via a wicking action in 5 s, and then easily immobilized into the film after 8 h conservation in humid atmosphere, providing therefore a novel approach to prepare antibacterial coating without any specific requirement for the characteristic of the agents. Scanning electron microscope was employed to show the dynamic transformation of film structures, from the original film with 9.5 nm of thickness to spongy sporous film with 68 nm of thickness and back to the solid film of 12 nm after the conservation process. Confocal scanning laser microscope image showed an even distribution of lysozyme in the film with lysozyme labelled by FITC. Loading quantity and the release dynamics of lysozyme were tested utilizing ultraviolet-visible spectrophotometer. Further, gram positive bacteria S. aureus and gram negative bacteria E. coli were tested in the antibacterial assay. The result illustrated that the coating was able to kill S. aureus efficiently, and the antibacterial activity of lysozyme was not affected by such loading and releasing process. To further enhance the bactericidal effect of the coating against gram negative bacteria, lysozyme and lactoferrin, which have synergistic killing effect on gram negative bacteria, were immobilized into the film at the same time and performed a distinct higher antibacterial efficiency against E. coli in comparison with the (PEI/PAA)(15)-lysozyme coating, revealing the attractive potential of this film as antibacterial coatings for medical devices to prevent the hospital-associated infections.

Antibacterial Activity of Nanofibrous Mats Coated with Lysozyme-Layered Silicate Composites Via Electrospraying.

Antimicrobial Application of Nanofibrous Mats Self-Assembled with Chitosan and Epigallocatechin Gallate.

Antimicrobial activity and cytotoxicity of nanofibrous mats immobilized with polysaccharides-rectorite based nanogels

Immobilization of Lysozyme on Layer-by-layer Self-Assembled Electrospun Nanofibers Treated by Post-Covalent Crosslinking

Poly(vinyl alcohol)/sodium alginate/layered silicate based nanofibrous mats for bacterial inhibition

Production of Thick Uniform-Coating Films Containing Rectorite on Nanofibers Through the Use of an Automated Coating Machine

Antibacterial multilayer films fabricated by layer-by-layer immobilizing lysozyme and gold nanoparticles on nanofibers

Enhanced bacterial inhibition activity of layer-by-layer structured polysaccharide film-coated cellulose nanofibrous mats via addition of layered silicate

Dynamic Spongy Microporous Films to Load Lysozyme for Antibacterial Coating

In-situ synthesis and immobilization of silver nanoparticles on microfibrillated cellulose for long-term antibacterial applications

One-Step Preparation of Carboxymethyl Cellulose/Polyoxyethylene Nanofiber Mats Containing Silver Nanoparticles

Antibacterial Coatings of Biomedical Surfaces by Polydextran Aldehyde/Polyethylenimine Nanofibers.

Long-term Antibacterial Activity by Synergistic Release of Biosafe Lysozyme and Chitosan from LBL-structured Nanofibers

Electrospraying Micro-Nano Structures on Chitosan Composite Coatings for Enhanced Antibacterial Effect

Immobilization of lysozyme on layer-by-layer self-assembled electrospun films: Characterization and antibacterial activity in milk

Chitosan/tannic acid bilayers layer-by-layer deposited cellulose nanofibrous mats for antibacterial application

Convenient Fabrication of Carboxymethyl Cellulose Electrospun Nanofibers Functionalized with Silver Nanoparticles

Silica-supported carboxylated cellulose nanofibers for effective lysozyme adsorption: Effect of macropore size

Chitosan-TiO2 microparticles LBL immobilized nanofibrous mats via electrospraying for antibacterial applications

Surface Modification of Polyacrylonitrile Nanofibrous Membranes with Superior Antibacterial and Easy-Cleaning Properties Through Hydrophilic Flexible Spacers

Optimization of lysozyme-modified ion exchange nanofiber membrane for efficient capture of Escherichia coli : Antibacterial and cytotoxic studies