Lamellar Morphology in Block Copolymers of Polystyrene and Poly[methyl(3,3,3-trifluoropropyl)siloxane]

Lingmin Yi,Xiaoli Zhan,Bi Chen,Bo Jiang
DOI: https://doi.org/10.1080/1539445x.2012.617643
2013-01-01
Soft Materials
Abstract:Well-defined polystyrene-block-poly[methyl(3,3,3-trifluoropropyl)siloxane] (PS-b-PMTFPS) diblock copolymers and polystyrene-block-poly[methyl(3,3,3-trifluoropropyl)siloxane]-block-polystyrene (PS-b-PMTFPS-b-PS) triblock copolymers with the volume fraction of PS between 0.46–0.61 were synthesized by anionic polymerization. The phase behavior and morphologies of the block copolymers were investigated via differential scanning calorimetry (DSC), rheological measurements, small-angle X-ray scattering (SAXS), and transmission electron microscopy (TEM). Equilibrium domain orientations of well-ordered lamellar microphase-separated structures were observed in the PS-b-PMTFPS diblock and PS-b-PMTFPS-b-PS triblock copolymer melts. The results showed that the synthesized block copolymers were desirable for achieving long-range order resulting from a high driving force between PS and PMTFPS blocks.
What problem does this paper attempt to address?