Al1.3FeCoNiCuCr HEA Coatings Produced by Laser Cladding

Cunyuan Peng,Mingxing Ma,Qiwen Wu,Wenjin Liu,Weiming Zhang
DOI: https://doi.org/10.2351/1.5063005
2013-01-01
Abstract:The Al1.3FeCoNiCuCr HEA coatings are produced by pre-placed laser cladding on 45steel substrate. The influence of processing parameters on the crack formation of the HEA coatings is inves tigated, so is the influence of the content of so me other elements. The experiments results showed that: The microstructure of the Al1.3FeCoNiCuCr is composed of dendrite and inter-dendrite. The microstructure consists of only fcc and bcc phases. The crack density of the Al1.3FeCoNiCuCr HEA coatings is 0.533mm/mm2 when the parameter is 3000W and 350mm/min. It decreases to 0.464mm/mm2 when the parameter changes to 3500W and 250mm/min. In both cases, the cracks run throughout the surface of the coating with the slag inclusion adhesion. On the other hand, with a 2wt.% addition of RE2O3 to the Al1.3FeCoNiCuCr HEA, the crack density decreases to 0.433mm/mm2. Furthermore, the throughout crack disappear and there only have some micro cracks in the interior of the coatings.
What problem does this paper attempt to address?