Large-scale Synthesis and Enhanced Visible-Light-driven Photocatalytic Performance of Hierarchical Ag/AgCl Nanocrystals Derived from Freeze-Dried PVP–Ag+ Hybrid Precursors with Porosity
Deliang Chen,Minna Liu,Qianqian Chen,Lianfang Ge,Bingbing Fan,Hailong Wang,Hongxia Lu,Daoyuan Yang,Rui Zhang,Qishe Yan,Guosheng Shao,Jing Sun,Lian Gao
DOI: https://doi.org/10.1016/j.apcatb.2013.07.042
2013-01-01
Abstract:To achieve high-performance, hierarchical plasmonic Ag/AgCl photocatalysts, a freeze-drying route was developed to form porous PVP-Ag+ hybrid compounds, which were then transformed to hierarchical Ag/AgCl nanocrystals through a liquid-solid precipitation reaction followed by a partially photoreduction under ambient conditions. The PVP-Ag+ hybrid precursors and their final Ag/AgCl nanocrystals obtained were characterized by various techniques. The hierarchical Ag/AgCl nanocrystals obtained had an apparent size range of 156 +/- 50 nm, and the surfaces of the large particles were covered with small nanocrystals with sizes of 33 +/- 12 nm. The photocatalytic performance of the hierarchical Ag/AgCl nanocrystals was estimated by degradating organic dyes (i.e., RhB, MO, and MB) and alcohols (i.e., methanol and isopropanol) under visible light (lambda >= 420 nm) and sunlight. The results indicated that the hierarchical Ag/AgCl nanocrystals obtained were efficient visible-light-driven photocatalysts in decomposing organic dyes, and their RhB photodegradation rates (similar to 0.97 min(-1)) was similar to 54 times higher than that (similar to 0.018 min(-1)) of TiO2 (P25) nanocrystals under the same visible-light conditions. The photodegradation efficiency of methanol and isopropanol reached similar to 45% and 35%, respectively, after visible-light irradiation for 60 min according to the COD data. The enhancement in visible-light-driven photodegradation performance results from the high absorbance through 350-800 nm due to the SPR effect of metal Ag species embedded in the hierarchical AgCl host nanocrystals. The influencing factors and possible growth mechanism of the Ag/AgCl nanooystals were investigated, and the PVP molecules and the freeze-drying process were highly influenced the size and morphology of Ag/AgCl nanocrystals. The outstanding advantage of the freeze-drying assisted route is its ability in large-scale synthesis of hierarchical Ag/AgCl nanocrystals. (C) 2013 Elsevier B.V. All rights reserved.