High-Performance Semitransparent Photodiodes Based on Zinc Oxide/C60/Copper Phthalocyanine Double Heterojunction
Yang Hu,Xiancheng Cao,Jiapei Huang,Jiawei Huang,Qiyue Zhang,Xiaoyue Xu,Ningbo Zhang,Xinyu Wang,Yingquan Peng,Wenli Lv,Sunan Xu,Lei Sun,Zhong Zhao,Lin Jiang
DOI: https://doi.org/10.1109/ted.2024.3395234
IF: 3.1
2024-05-25
IEEE Transactions on Electron Devices
Abstract:Photovoltaic devices based on metal oxide and organic semiconductor heterostructure generally exhibit poor performance due to inefficient exciton dissociation at the metal oxide/organic interface. Here, we present an enhancement in the performance of photodiodes fabricated via zinc oxide (ZnO)/C60/copper phthalocyanine (CuPc) double heterojunction solution. This obtained photodiode demonstrates photodetection in the wavelength range of 400–850 nm with high photoresponsivity (R), specific detectivity ( ), and transparency. Remarkably high R of 9040, 64.0, and 2.0 A/W and of , , and Jones were achieved, for representative wavelengths of 405, 650, and 850 nm, respectively. The device exhibited a maximal average, transparency of 0.444 in the wavelength range of 400–1000 nm. Investigation into the effects of C60 layer thickness ( ) revealed a strong dependence of both R and on . For shorter wavelengths (405 and 450 nm), the maxima of curves were observed around nm, whereas for longer wavelengths (532, 650, and 850 nm), they appeared at around nm. The maxima of curves were consistently located at nm for all measured wavelengths. Further investigations on the impact of CuPc layer thickness ( ) indicated that the device achieved maximal R and at nm for light of wavelength 405 and 450 nm, and at 40 nm for light of wavelength 650 and 780 nm. Specifically, for the light of wave-length 532 nm, R was maximal at nm, while peaked at nm. Moreover, optical simulations partially elucidated the physical origin behind these results. The obtained results provide an effective strategy to fabricate high-performance semitransparent photodiodes.
engineering, electrical & electronic,physics, applied