Abstract:A novel synthetic strategy has been adopted to deposit Au nanoparticles (NPs) (ca. 5 nm) on a hollow FeOx substrate using Au/beta-FeOOH hybrid nanocrystals as the precursor. Through the encapsulation of Au/beta-FeOOH by SiO2 shells and the calcination step, the Au/beta-FeOOH can be transformed into Au/FeOx with the hollow structural feature. Because of the protective SiO2 shells, aggregation of the Au NPs is effectively prohibited, and the hemispherical morphology of the Au particles is essentially retained. The Au/FeOx hollow composite is obtained by removing the SiO2 shells, and the Au NPs in the final Au/FeOx hollow composite are small-sized yet stable enough because of the calcination history. The derived Au/FeOx hollow composite shows a substantial pretreatment effect on CO oxidation: with a pretreatment in the reaction feed at 180 degrees C for 0.5 h, the hollow Au/FeOx shows the T-100 of CO oxidation decreasing from 180 to 88 degrees C. O-2 temperature-programmed desorption and X-ray photoelectron spectroscopy characterizations revealed that the pretreatment may result in (i) the creation of electron holes in the p-type FeOx substrate and electron deficiency of Au nanoparticles as well as a strong Au-FeOx interaction; (ii) appropriate coverage of oxygen adspecies on the Au NPs; and (iii) increased surface oxygen density, especially at the Au-FeOx boundary region, as a result of the spillover effect of oxygen adspecies from Au NPs. All of these features are responsible for an overall enhanced activity of CO oxidation and better durability of the Au/FeOx hollow composite.

Half-encapsulated Au Nanoparticles by Nano Iron Oxide: Promoted Performance of the Aerobic Oxidation of 1-Phenylethanol

Synthesis, Characterizations and Catalytic Performance of Nanostructure Au/Fe2O3

Gold Nanoparticles on Electroless-Deposition-derived MnOx/C: Synthesis, Characterization, and Catalytic CO Oxidation

Substantial Pretreatment Effect on CO Oxidation over Controllably Synthesized Au/FeOx Hollow Nanostructures Via Hybrid Au/β-FeOOH@SiO2

A Rational Solid-State Synthesis of Supported Au-Ni Bimetallic Nanoparticles with Enhanced Activity for Gas-Phase Selective Oxidation of Alcohols.

Superior Catalytic Properties in Aerobic Oxidation of Alcohols over Au Nanoparticles Supported on Layered Double Hydroxide

Supported Gold Nanoparticles as Catalysts in Peroxidative and Aerobic Oxidation of 1-Phenylethanol under Mild Conditions

Highly Active Gold Catalysts Loaded on NiAl-oxide Derived from Layered Double Hydroxide for Aerobic Alcohol Oxidation

Boosted formic acid electro-oxidation on platinum nanoparticles and "mixed-valence" iron and nickel oxides

Au Nanoparticles Supported on a Layered Double Hydroxide with Excellent Catalytic Properties for the Aerobic Oxidation of Alcohols

Mg‐Al Mixed Oxides Supported Bimetallic Au‐Pd Nanoparticles with Superior Catalytic Properties in Aerobic Oxidation of Benzyl Alcohol and Glycerol

Engineering Pt Nanoparticles onto Resin‐Derived Iron and Nitrogen Co‐Doped Porous Carbon Nanostructure Boosts Oxygen Reduction Catalysis

Interfacial Effects in Iron-Nickel Hydroxide–Platinum Nanoparticles Enhance Catalytic Oxidation

A novel core-shell nanostructure of Ti-Au nanocrystal with PtNi alloy skin: Enhancing the durability for oxygen reduction reaction

Pre-deposited Co nanofilms promoting high alloying degree of Pd Au nanoparticles as electrocatalysts in alkaline media

Synthesis of Gold Nanoparticles over CoAl Mixed Oxide for Ethanol Oxidation Reaction

Influence of hematite morphology on the CO oxidation performance of Au/α-Fe2O3

Aerobic Homocoupling of Phenylboronic Acid on Mg–Al Mixed-Oxides-supported Au Nanoparticles

Fe3O4 Nanoparticles Encapsulated in Single-Atom Fe–N–C Towards Efficient Oxygen Reduction Reaction: Effect of the Micro and Macro Pores

Progress in Catalytic Oxidations over Supported Au Nano-Particle Catalyst

Iron Nanoparticles Encapsulated in S,N-Codoped Carbon: Sulfur Doping Enriches Surface Electron Density and Enhances Electrocatalytic Activity Toward Oxygen Reduction.