Effect of aging temperatures on the microstructure and mechanical properties of TC21 forgings with basket–weave microstructure
Xiang Li,Chaowen Huang,Xianwei Ye,Jiang Yang,Mingpan Wan,Dan Liu
DOI: https://doi.org/10.1016/j.matchar.2024.114270
IF: 4.537
2024-08-19
Materials Characterization
Abstract:This study aims to explore the influence of various aging temperatures on the microstructure and mechanical properties of TC21 forgings. Basket-weave microstructures were prepared via quasi-β forging followed by annealed at 900 °C for 1.5 h and aged at 530 °C, 560 °C, and 590 °C for 4 h, and then their tensile performance, impact toughness, and fracture toughness were examined. Results indicate that higher aging temperatures not only facilitate the segregation of Al element, resulting in a reduction in the effective size (dα laths , the width/length ratio) of primary α laths (α laths ) and their amount, but also promote phase transition, inducing an increase in the effective size (dα fine ) of secondary fine α (α fine ) lamellae. While both dα laths −1/2 and dα fine −1/2 have a linear relationship with the strength, which was analyzed using the Hall–Petch relationship, the more pronounced interface strengthening effect and hindering crack propagation mainly results from the α laths . Moreover, the plasticity declines significantly as the proportion of the α laths phases decreases. Thus, for strength and plasticity, the α laths are a much more important factor than the α fine lamellae. However, although the synergistic deformation and fracture of both the α laths and α fine phases can consume a larger impact initiation energy, the enhancement of the impact energy of the alloy is primarily related to a high precipitation amount of the α fine lamellae. Furthermore, the decrease in dα laths promotes the misorientation and accumulation of dislocations between α laths interfaces, hindering the enhancement of K IC (fracture toughness) by forming transgranular fractures. Conversely, the increase in K IC attributed to the energy consumed in the plastic deformation region at the crack tip, due to the α fine lamellae compensates for the energy, resulting in a reduction in the crack propagation path. Therefore, the α fine lamellae may play a more crucial role in increasing the toughness of alloys, in particular the impact toughness of the TC21 alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing