Abstract:PtCu alloy nanocrystals, especially for the PtCu3 component, hold great potential as catalysts in methanol oxidation reaction (MOR) owing to their promising catalytic properties arising from the bifunctional mechanism associated with Pt and Cu sites. However, Pt and Cu salt precursors are difficult to be co-reduced in a synthesis due to the large difference in their redox potential, because of which Pt or Cu nanocrystals are initially generated and then evolve into a PtCu alloy with remarkable variation of the PtCu component by underpotential deposition (UPD) and galvanic replacement, respectively. Here we report a facile method for the shape-controlled synthesis of PtCu3 alloy nanocrystals by co-reduction of Pt and Cu salt precursors using oleylamine (OAm) and N,N-dimethylformamide (DMF) as co-reducing agents at different temperatures. PtCu3 alloy hexapods with preferential overgrowth along the <100> direction are obtained at 220 degrees C through co-reduction reaction accompanied by Cl- ion induced underpotential deposition (UPD). Meanwhile, galvanic replacement between PtCu3 alloy nanocrystals and the Pt precursor co-exists with overgrowth induced by co-reduction reaction at 190 degrees C, eventually resulting in PtCu3 hollow nanoframes. Both the PtCu3 alloy hexapods and hollow nanoframes exhibit remarkably enhanced catalytic properties in terms of activity and stability towards MOR relative to the commercial Pt/C. Specifically, the PtCu3 alloy hexapods and hollow nanoframes show the highest specific (2.96 mA cm(-2)) activity and mass activity (1.861 mA mu g(Pt)(-1)) for MOR, respectively, which are 13.5 and 24.2 times higher than those of the commercial Pt/C. This enhancement can be attributed to their unique structures and the possible bifunctional mechanism between Pt and Cu.

Facile Synthesis of Pd-based Bimetallic Nanocrystals and Their Application As Catalysts for Methanol Oxidation Reaction

PdCu Alloy Nanodendrites with Tunable Composition As Highly Active Electrocatalysts for Methanol Oxidation

Facile Synthesis of Pd@PtM (<i>M</i> = Rh, Ni, Pd, Cu) Multimetallic Nanorings as Efficient Catalysts for Ethanol Oxidation Reaction

Facile synthesis of Pd-Pt alloy concave nanocubes with high-index facets as electrocatalysts for methanol oxidation

Pd-on-NiCu Nanosheets with Enhanced Electro-Catalytic Performances for Methanol Oxidation

Facile Synthesis of Ternary PtPdCu Alloy Hexapods As Highly Efficient Electrocatalysts for Methanol Oxidation

Facile Synthesis of Ptcu3 Alloy Hexapods and Hollow Nanoframes As Highly Active Electrocatalysts for Methanol Oxidation

Pt Nanoparticles Dispersed on Ni/C Nanoflowers As Stable Electrocatalysts for Methanol Oxidation and Oxygen Reduction

Supported Pd-Cu bimetallic nanoparticles that have high activity for the electrochemical oxidation of methanol.

Tuning Surface Structure of Pd3Pb/PtnPb Nanocrystals for Boosting the Methanol Oxidation Reaction

One-step Synthesis of the PdPt Bimetallic Nanodendrites with Controllable Composition for Methanol Oxidation Reaction

Supported Bimetallic PdAu Nanoparticles with Superior Electrocatalytic Activity Towards Methanol Oxidation

Monodispersed bimetallic PdAg nanoparticles with twinned structures: Formation and enhancement for the methanol oxidation

Preparation of PdNi nanospheres with enhanced catalytic performance for methanol electrooxidation in alkaline medium

Component-dependent Activity of Bimetallic PdCu and PdNi Electrocatalysts for Methanol Oxidation Reaction in Alkaline Media

Facile synthesis of Pt/Pd nanodendrites for the direct oxidation of methanol.

Preparation of Nanoporous Pd/Cuo by Dealloying and Their Electrocatalysis for Methanol in Alkaline Condition

PtPdRh Mesoporous Nanospheres: an Efficient Catalyst for Methanol Electro-Oxidation

A Facile One-Step Preparation of a Pd–Co Bimetallic Hollow Nanosphere Electrocatalyst for Ethanol Oxidation

Enhanced Electrocatalytic Activity of Palladium Nanochains by Modifying Transition Metal Core-Shell Nanoparticles (Tmcore-Shell = Ni@NiO, Co@CoO) on Reduced Graphene Oxide for Methanol Electro-Oxidation

Three-dimensional PdCuM (M = Ru, Rh, Ir) Trimetallic Alloy Nanosheets for Enhancing Methanol Oxidation Electrocatalysis.