Morphotropic Phase Boundary, Polymorphic Phases and Enhanced Electrostrain/piezoelectricity in Ag1-xKxNbO3 Solid-Solution Ceramics
Ye Tian,Ye Jia,Xinyi Wang,Lei Li,Jia Geng,Tong Wang,Yonghao Xu,Li Jin,Yizheng Bao,Chen,Leiyang Zhang,Ming Ma,Xiaoyong Wei,Wanyin Ge
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.03.031
IF: 5.7
2023-01-01
Journal of the European Ceramic Society
Abstract:Ag1_xKxNbO3(AKNx (x <= 0.12) ceramics were prepared to understand the relationship of structure-properties driven by compositions and temperatures. The results suggested that this binary system possessed a morpho-tropic phase boundary (MPB) consisted of ferrielectric and ferroelectric phases with iso-symmetry at room temperature, in which domains switching together with electric-field-induced irreversible phase transition achieved a much higher electrostrain (Smax= 0.4%) than other compositions. But this MPB was destroyed after poling, leading to inferior piezoelectricity. A phase diagram was drawn after analyzing in situ XRD and dielectric data, where an almost vertical ferrielectric/antiferroelectric <-> polymorphic ferroelectric MPB line starting from a triple point was proposed. As temperature increased, the piezoelectricity significant enhanced near ferroelectric orthorhombic <-> monoclinic phase boundary, while the highest piezoelectricity was achieved near the mono-clinic <-> paraelectric phase boundary with d33 = 200 pC/N. The enhanced piezoelectricity is intimately related to the ferroelectric monoclinic possessing Pm symmetry.