Construction of oxygen vacancies and heterostructure in VO 2-x /NC with enhanced reversible capacity, accelerated redox kinetics, and stable cycling life for sodium ion storage
Baolin Liu,Hongyu Zhang,Chun Yuan,Qin Geng,Yizhao Li,Jindou Hu,Zhenjiang Lu,Jing Xie,Aize Hao,Yali Cao
DOI: https://doi.org/10.1016/j.jcis.2023.05.047
IF: 9.9
2023-05-14
Journal of Colloid and Interface Science
Abstract:Developing anode materials with high reversible capacity, fast redox kinetics, and stable cycling life for Na + storage remains a great challenge. Herein, the VO 2 nanobelts with oxygen vacancies supported on nitrogen-doped carbon nanosheets (VO 2-x /NC) were developed. Benefitting from the enhanced electrical conductivity, the accelerated kinetics, the increased active sites as well as the constructed 2D heterostructure, the VO 2-x /NC delivered extraordinary Na + storage performance in half/full battery. Theoretical calculations (DFT) demonstrated that oxygen vacancies could regulate the adsorption ability for Na + , enhance electronic conductivity, as well as achieve rapid and reversible Na + adsorption/desorption. The VO 2-x /NC exhibited high Na + storage capacity of 270 mAh g −1 at 0.2 A g −1 , and impressive cyclic stability with 258 mAh g −1 after 1800 cycles at 10 A g −1 . The assembled sodium-ion hybrid capacitors (SIHCs) could achieve maximum energy density/power output of 122 Wh kg −1 /9985 W kg −1 , ultralong cycling life with 88.4% capacity retention after 25,000 cycles at 2 A g −1 , and practical applications (55 LEDs could be actuated for 10 min), promising to be utilized in a practicable Na + storage.
chemistry, physical