Abstract:A series of K-ZrO2/Cu/Al2O3 catalysts (KZC(T)A (T= 600-900 degrees C)) were prepared by a sequential impregnation method and investigated for the direct synthesis of ethanol and isobutanol from syngas. The calcination temperature for C(T)A (T= 600-900 degrees C) preparation had considerable effect on the structure and catalytic performance of KZCTA catalysts. By increasing the calcination temperature from 600 to 900 degrees C, the CO conversion was promoted obviously from 20.3 to 53.0%. When the calcination temperature was lower, KZC(700)A catalyst showed high isobutanol selectivity of 17.7 wt%, while only a small amount of isobutanol was obtained in the reference catalysts of KZA and KC(700)A without Cu or Zr as promoters. The coexistence of Cu and Zr in the catalyst was required for isobutanol formation. Furthermore, the Cu-ZrO2 interface amounts increased firstly with the increase of calcination temperature and then decreased at over-higher calcination temperature because of the aggregation of ZrO2. The isobutanol selectivity changed with the Cu-ZrO2 interface amounts in catalyst, suggesting that the Cu-ZrO2 interfaces were responsible for isobutanol preferable synthesis directly from syngas. In addition, ethanol selectivity increased clearly up to 36.3 wt% when the higher calcination temperature 900 degrees C was employed for catalyst preparation. In comparison with the KZC(900)A catalyst, the catalyst of KC(900)A prepared without Zr as promoter exhibited excellent catalytic performance for the ethanol synthesis (33.5 wt%). It revealed that Zr cannot contribute to ethanol formation, and the newly formed CuAlO2 phase under higher calcination temperature in the catalysts possibly favored ethanol formation. As confirmed by XRD, Raman spectroscopy and H-2-TPR, the CuAlO2 phase emerged and its amount increased with the increase of calcination temperature for catalyst preparation. A good linear relationship was found between ethanol selectivity and the amount of CuAlO2, proving that the CuAlO2 phase acted as efficient active sites for ethanol preferable synthesis directly from syngas.

Surface Structural Evolution of Auag/Tio2 Catalyst in the Transformation of Benzyl Alcohol to Sodium Benzoate

Enhanced Performance of Binary WO3/N-doped Carbon Composites for the Catalytic Oxidation of Benzyl Alcohol under Mild Conditions

Synthesis of Au-CeO2/SiO2 catalyst via adsorbed-layer reactor technique combined with alcohol-thermal treatment

Preparation and Catalytic Activity of Au-Ag Bimetallic Catalyst for Cyclohexane Oxidation

Bimetallic Gold-Silver Nanoparticles Supported on Zeolitic Imidazolate Framework-8 as Highly Active Heterogenous Catalysts for Selective Oxidation of Benzyl Alcohol into Benzaldehyde

One-pot solvent-free synthesis of sodium benzoate from the oxidation of benzyl alcohol over novel efficient AuAg/TiO 2 catalysts

The Effect of Calcination Temperature on the Structure and Activity of TiO2/SiO2 Composite Catalysts Derived from Titanium Sulfate and Fly Ash Acid Sludge

Effect of Calcination Temperature on the Catalytic Activity of Nanosized TiO2 for Ozonation of Trace 4-Chloronitrobenzene

Preparation and Application of Metal Oxides/SBA-15 Mesoporous Composites as Catalysts for Selective Oxidation of benzyl alcohol

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Effects of Calcination Temperature on Structure-Activity of K-ZrO2/Cu/Al2O3 Catalysts for Ethanol and Isobutanol Synthesis from CO Hydrogenation

Surface Acidic and Redox Properties of V–Ag–O/TiO 2 Catalysts for the Selective Oxidation of Toluene to Benzaldehyde

Low-temperature, Highly Selective, Gas-Phase Oxidation of Benzyl Alcohol over Mesoporous K-Cu-TiO2 with Stable Copper(i) Oxidation State.

Preparation of Mesoporous Supported CuCo2O4 Catalyst and Selective Oxidation of Benzyl Alcohol

Study on catalytic synthesis of flavor isobutyl benzoate using nanometer TiO2 as catalyst

Tuning the oxygen vacancy and acidity of V-Ag-Ce/TiO 2 catalyst for selective gas-phase oxidation of toluene to benzaldehyde

Dynamic Transformation of Active Components in Cu-ZnO-Al_2O_3 Catalyst for Methanol Synthesis at High Temperature

Synergistic effect on Au-Pd bimetallic catalyst during oxidation of benzyl alcohol to sodium benzoate

Selective Aerobic Oxidation of Benzyl Alcohol Driven by Visible Light on Gold Nanoparticles Supported on Hydrotalcite Modified by Nickel Ion

Low‐Temperature Gas‐Phase Oxidation of Benzyl Alcohol on Mesoporous K‐Cu‐TiO2 Through Oxidative Dehydrogenation

Highly Dispersed Gold Nanoparticles Supported on SBA-15 for Vapor Phase Aerobic Oxidation of Benzyl Alcohol