Abstract:A series of NaGd(0.99-x%)F4: 1% Bi3+, x% Eu3+ (x = 0-50) and NaGd(1-x%)F4: x% Eu3+ (x = 0-50) nanocrystals (denoted as NGBF-x% Eu3+ and NGF-x% Eu3+, respectively) have been synthesized by hydrothermal method. The influence of Bi3+ and Eu3+ on microstructures and luminescence properties of the products are deeply investigated. The TEM results display that all the obtained products are irregular polyhedrons with a diameter in a range from 30 to 80 nm with the increasing substitution concentration of Eu3+. It was found that the introduction of Bi3+ hardly affects the morphology and size of the obtained products. Under the excitation of 393 nm NUV, all samples exhibit the typical emission of Eu3+ ions with main red and yellow emissions centered at 616 and 591 nm, respectively. After doping a small amount of Bi3+ ions, the largest emission intensity of the characteristic emissions of Eu3+ for the gained NGBF-x% Eu3+ nanocrystals appeared at x = 0.2, whereas it observed at x = 0.3 for the obtained NGF-x% Eu3+ nanocrystals. It is obviously that the introduction of 1% Bi3+ ions not only increases the emission intensity of Eu3+ ions significantly, but also reduces the doping concentration of Eu3+. Especially, studied NGBF-20% Eu3+ phosphor exhibits excellent stand up to thermal impact during thermal cycling between 298 and 473 K. A WLED device by merging a NUV chip, NGBF-20% Eu3+ phosphor and commercial (Sr,Ba)(2)SiO4: Eu2+ green phosphor/BaMgAl10O17: Eu2+ blue phosphor possesses suitable correlated color temperature (CCT, 7395 K) and high color rendering index (CRI, 90.8%). These results unambiguously show that the NGBF-x%Eu3+ nanocrystals are promising candidate for applications in WLEDs. (C) 2020 Elsevier B.V. All rights reserved.

Nanophosphors Eu3+-Doped BiPO4: Roomerature synthesis and optimum luminescence properties

Hydrothermal synthesis, microstructure and luminescence properties of BiPO4:Eu3+ phosphor

Luminescence Behavior of Eu3+ Doped LaF3 Nanoparticles.

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Synthesis and Luminescence Properties of Eu3+ Doped High Temperature Form of Bi2MoO6

Intense photoluminescence and mechanoluminescence of novel BaLaAl3O7:xEu3+ red nanophosphors

Luminescence Properties and Dynamical Processes of Energy Transfer in BiPO4: Tb3+,Eu3+ Phosphor

Luminescence properties, tunable emission and energy transfer of Ca9MgLi(PO4)7:Bi3+/Eu3+ phosphor

Photoluminescence characteristics and energy transfer between Bi 3+ and Eu 3+ in Gd 2 O 3 : Eu 3+ , Bi 3+ nanophosphors

Photoluminescence Characteristics and Energy Transfer Between Bi3+ and Eu3+ in Gd2o3: Eu3+, Bi3+ Nanophosphors

Photoluminescence Characterization of Ca10Na(PO4)7:Eu3+ Red-Emitting Phosphor.

Sol–gel Preparation and Photoluminescence Enhancement of Li+ and Eu3+ Co-Doped YPO4 Nanophosphors

The room temperature photoluminescence properties of Eu 3+ -doped bi-phase calcium phosphate under visible light

Bi3+ Ion Doping: an Effective Strategy to Significantly Enhance Luminescence Performances of NaGdF4: Eu3+ Red-Emitting Nanocrystals

Adjustable luminescence properties of Eu3+ and Bi3+ codoped Ca3Zn3Te2O12 phosphor

Comparative Study of Ca3Bi(PO4)3:Eu3+ Phosphors Prepared by Three Methods

Synthesis and Luminescence Properties of (Y, Gd) (P, V)O4:Eu3+, Bi3+Red Nano-phosphors with Enhanced Photoluminescence by Bi3+, Gd3+ Doping

Luminescence Investigation of Eu~(3+)-Bi~(3+) Co-Doped CaMoO_4 Phosphor

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Improvement of Luminescence Performance of Single-Phase White-Emitting Na3Gd(PO4)2:Dy3+ Phosphor by Co-Doping with Eu3+

LaPO4:Eu3+, LaPO4:Ce3+, and LaPO4:Ce3+,Tb3+ nanocrystals: Oleic acid assisted solvothermal synthesis, characterization, and luminescent properties