One-step fabrication of TiO2/graphene hybrid mesoporous film with enhanced photocatalytic activity and photovoltaic performance
Junxiong Guo,Yiyi Li,Shangdong Li,Xumei Cui,Yu Liu,Wen Huang,Linna Mao,Xiongbang Wei,Xiaosheng Zhang
DOI: https://doi.org/10.1016/s1872-2067(19)63511-4
IF: 16.5
2020-08-01
Chinese Journal of Catalysis
Abstract:We synthesized a mesoporous film based on TiO<sub>2</sub>–reduced graphene oxide (RGO) hybrids using a one-step vapor-thermal method without the need for an additional annealing process. The vapor-thermally prepared TiO<sub>2</sub>-graphene hybrid (VTH) features unique structures with an ultra-large specific surface area of ˜260 m<sup>2</sup> g<sup>−1</sup> and low aggregation, giving rise to enhanced light harvesting and increased charge generation and separation efficiency. It was observed that a mesoporous film with uniform pore distribution is simultaneously obtained during the VTH growth process. When a 5.0 wt% RGO VTH film was used as the active layer in photocatalysis, the highest photocatalytic activity for degradation of methyl orange was achieved. For another, when a 0.75 wt% RGO VTH film was used as the photoanode in a dye-sensitized solar cell, the power conversion efficiency reached 7.58%, which represents an increase of 73.1% compared to a solar cell using an a photoanode of pure TiO<sub>2</sub> synthesized by a traditional solvothermal method. It is expected that this facile method for the synthesis of TiO<sub>2</sub>/graphene hybrid mesoporous films will be useful in practical applications for preparing other metal oxide/graphene hybrids with ultra-high photocatalytic activity and photovoltaic performance.A mesoporous film based on TiO<sub>2</sub>-reduced graphene oxide hybrids was fabricated using a one-step vapor-thermal method, which exhibits an ultra-high photocatalytic activity and enhanced photovoltaic performance.
chemistry, physical,engineering, chemical, applied