Tribological Performance of DLC Coatings Deposited by Ion Beam Deposition under Dry Friction and Oil Lubricated Conditions

Fu Zhiqiang,Sun Jian,Wang Chengbiao,Zhang Wei,Yue Wen,Peng Zhijian,Yu Xiang,Lin Songsheng,Dai Mingjiang

DOI: https://doi.org/10.1016/j.vacuum.2013.01.006

IF: 4

2013-01-01

Vacuum

Abstract:Understanding the reaction between lubricant additives and diamond-like carbon coatings is imperative for the improvement of the friction and wear properties of mechanical parts with diamond-like carbon coatings. Diamond-like carbon coatings were deposited with ion beam deposition and the influence of lubricant additives on the friction coefficients and wear rates of diamond-like carbon coatings under the lubricated conditions was studied. It was revealed that the wear rates of diamond-like carbon coatings under unlubricated conditions are 1.5 x 10(-14) m(3)/(Nm) while they are decreased to 3 x 10(-17) m(3)/(Nm) to 1.7 x 10(-16) m(3)/(Nm) when lubricated by PAO-4 base oil with three additives. The addition of molybdenum dithiocarbamate in PAO-4 base oil decreases the friction coefficients of diamond-like carbon coatings to 0.07, but increases the wear rate of diamond-like carbon coatings. The addition of zinc dialkyl dithiophosphate to PAO-4 can slightly decrease the friction coefficient of diamond-like carbon coatings and improve the wear resistance of diamond-like carbon coatings. The addition of amine sulfuric-phosphate diester in PAO-4 can greatly decrease the wear rate of diamond-like carbon coatings to 3 x 10(-17) m(3)/(Nm) but has a negligible effect on the friction coefficients of diamond-like carbon coatings. (C) 2013 Published by Elsevier Ltd.