Abstract:The dechlorination of HCB was carried out under low-temperature and oxygen deficient conditions on different solid supports such as SiO2, CaO, CaSiO3, cement and treated fly ash (tFA). All the tested supports except SiO2 showed a HCB dechlorination potential. The dechlorination efficiencies (D1) of HCB by CaO, CaSiO3, tFA and cement reached 64.62%, 76.15%, 79.97% and 32.21% at 350°C for 4h, respectively. It was thought electrons in the vacancies originated from the unsaturated metallic ions and O2− on the crystal surfaces made the D1 different between SiO2, CaO and CaSiO3. Comparing the D1 by tFA and cement, the high dechlorination potential of tFA was due to the more free electrons from the crystal defects and the transition metals, and the more active points for the gas–solid phase reaction, which both had positive effects on dechlorination reaction. The effect of Cu addition (0.2–5.0%) on HCB dechlorination might result from the Ullmann coupling which was not notable in enhancing the dechlorination reaction. From the study, we can draw the conclusion that the dechlorination potential mainly depends on the support characteristic rather than the transition metal content. Based on this study and previous references, the dechlorination/polymerization induced by the electron transfer mode was thought to be the dominant pathway while the hydrogen transfer mode was minor. The electron was originated from the crystal defects or induced by transition metals, and the dissociation of a chloride ion happened forming a radical, and then the polymerization of radicals led to the formation of high-molecular-weight compounds which seemed to cause the material imbalance.

[Dechlorination of HCB by Bimetals Based on Zero Valent Iron].

Dechlorination of Hexachlorobenzene Using Lead–iron Bimetallic Particles

Study on Dechlorination Capabilities of Zero-valent Iron,Nickel-Iron or Copper-Iron Bimetal on Tetrachloroethylene

Effective dechlorination of HCB by nanoscale Cu/Fe particles.

Subcolloidal Fe/Ag Particles for Reductive Dehalogenation of Chlorinated Benzenes

Dechlorination of hexachlorobenzene by nano zero-valent iron/activated carbon composite: iron loading, kinetics and pathway

Effect of Cu on the Reductive Dechlorination of Chlorinated Hydrocarbons in Water by Scrap-Iron

Rapid Degradation of Hexachlorobenzene by Micron Ag/Fe Bimetal Particles.

Reductive dechlorination of hexachlorobenzene by Cu/Fe bimetal in the presence of nonionic surfactant.

Dechlorination of P-Dichlorobenzene by Metallic Catalytic Reduction Technology

Reductive dehalogenation of brominated disinfection byproducts by iron based bimetallic systems

Dechlorination of Excess Trichloroethene by Bimetallic and Sulfidated Nanoscale Zero-Valent Iron

Base-catalyzed Destruction of Hexachlorobenzene with Zero-Valent Iron

Surfactant Mediated HCB Dechlorination in Contaminated Soils and Sediments by Micro and Nanoscale Cu/Fe Particles

Synergic effect of calcium oxide and iron (III) oxide on the dechlorination of hexachlorobenzene.

Dechlorination of hexachlorobenzene using ultrafine Ca-Fe composite oxides.

Mechanism and Influence Factors of 2,4‐D Dechlorination by Sodium Citrate‐activated Bimetallic Palladium‐zero Valent Iron Nanoparticles

Synthesis of monodispersed CMC-stabilized Fe-Cu bimetal nanoparticles for in situ reductive dechlorination of 1,2,4-trichlorobenzene.

Dechlorination of 2,2′,4,4′,5,5′-Hexachlorobiphenyl by Thermal Reaction with Activated Carbon-Supported Copper or Zinc

Low-temperature dechlorination of hexachlorobenzene on solid supports and the pathway hypothesis.

Dechlorination of tetrachloroethene with nanoscale Ni/Fe and Cu/Fe bimetallic particles