On the Friction Behavior of SiO 2 Tip Sliding on the Au(111) Surface: How Does an Amorphous SiO 2 Tip Produce Regular Stick–Slip Friction and Friction Duality?
Rong-Guang Xu,Gunan Zhang,Yuan Xiang,Yongsheng Leng
DOI: https://doi.org/10.1021/acs.langmuir.3c00237
IF: 3.9
2023-04-24
Langmuir
Abstract:Friction behaviors of an amorphous SiO<sub>2</sub> tip sliding on the Au(111) surface in atomic force microscopy (AFM) are investigated through molecular dynamics (MD) simulations. We observed a regime of extremely low, close-to-zero friction at low normal loads with clear stick-slip friction signals. The friction is almost independent of the applied normal load below a threshold value. However, above this loading threshold, friction can remain low or increase sharply. Such an unexpected friction <i>duality</i> is attributed to the high probability of defect formation at the sliding interface that can induce plowing friction in a high-friction state. The energy difference between the low-friction state and the high-friction state is surprisingly low, which is comparable to kT (∼25 meV) at room temperature. These findings are consistent with previous AFM friction measurements using silicon AFM tips. Further MD simulations show that one can always use an amorphous SiO<sub>2</sub> tip to image the crystalline surface with regular stick-slip friction signals. This is largely due to the fact that there is always a small fraction of contacting Si and O atoms at the sliding interface that are sitting on the relatively stable, close-to-hollow sites of the crystalline Au(111) surface during the stick stage; thus, they are capable of sampling local energy minima. We anticipate that regular stick-slip friction can be achieved even in the intermediate loading range, so long as the low-friction state is maintained when friction duality occurs.
chemistry, multidisciplinary, physical,materials science