Abstract:Most spinel-structured materials of negative temperature coefficient (NTC) contain Ni, which have high cost. In this work, Ni-free Zn 0.9 Cu x Mn 2.1- x O 4 (0.1 ≤ x ≤ 0.5) NTC material system is developed. X-ray diffraction (XRD) spectra show that Zn 0.9 Cu x Mn 2.1- x O \ intered at 1100 °C crystallizes in a tetrahedral spinel structure, which is caused by the Jahn-Teller effect of the Mn 3+ ions at the B sites. Cu2p 3/2 X-ray photoelectron spectra (XPS) demonstrate that most of Cu ions located at B sites are at the valance of 2+. The resistivity of Zn 0.9 Cu x Mn 2.1- x O 4 varies from 1,340 Ω cm to 51,489 Ω cm, and B value from 3,357 K to 4,276 K. The resistivity drift after annealing at 150 °C in air for 1,000 h is less than 3 % which is stable enough for practical application.

Spinel-structured Ni-free Zn 0.9 Cu x Mn 2.1- x O 4 (0.1 ≤ x ≤ 0.5) thermistors of negative temperature coefficient