Abstract:We investigate the structural, dielectric relaxation, electric modulus and impedance behavior of Ni-doped NASICON ceramic Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) prepared using the solid-state reaction method. The increase in dielectric constant with temperature and decrease with frequency is explained on the basis of space charge polarization using the two-layer model of Maxwell-Wagner relaxation. The dielectric loss peak at lower temperatures follows the Arrhenius-type behavior with frequency having activation energy of 0.27$\pm$0.01~eV of dipolar relaxation, suggests similar type of defects are responsible for all the doped samples. The real ($\epsilon$ $^{'}$) and imaginary ($\epsilon$ $^{''}$) permittivity variation with frequency shows the broad relaxation behavior indicates the non-Debye type of relaxation in the measured temperature range. The permittivity values decrease with the amount of doping due to the increased number of charge carriers upon Ni doping at the Zr site. The grain contributions are observed at higher frequencies, while grain-boundary contributions occur at the lower side of frequencies. The imaginary part of the electric modulus also shows two types of relaxation peaks for all the samples indicating similar activation energy at low temperatures and variable activation energy at higher temperatures. The fitting of the imaginary modulus using KWW function shows the non-Debye type of relaxation. We find that all modulus curves merge with each other at low temperatures showing a similar type of relaxation, while curves at high temperatures show the dispersed behavior above the peak frequency. The {\it a.c.} conductivity data are fitted using the double power law confirming the grain and grain boundary contributions in total conductivity.

The Equivalent Circuits for Polaronic Relaxation: Taking the LaNi3/4Mo1/4O3 As a Model Sample

Low Temperature Dielectric Relaxation in Complex Perovskite Bati0.8(Ni0.5nb0.5)(0.2)O-3 Ceramics

Polaronic Relaxation in La0.8bi0.2fe0.7mn0.3o3

Polaronic Relaxation in Lafeo3

Dielectric Relaxations in Multiferroic La2ti2o7 Ceramics

Polaron Relaxation Related to Localized Charge Carriers in Pr1−xCaxMnO3

Relaxor-like dielectric behavior in La2NiMnO6 double perovskite ceramics

Dielectric Relaxation and Polaronic Hopping in Al-substituted Sm1.5Sr0.5NiO4 Ceramics

Polaronic Relaxation in Ca2timno6 at Low Temperatures

Dielectric relaxation and polaronic hopping in Al-substituted Sm 1.5Sr0.5NiO4 ceramics

Phase Separation Inla2cuo4+yceramics Probed by Dielectric Measurements

Conductivity relaxation in NiTiO3 at high temperatures

Dielectric Relaxation and Polaronic Hopping in the Single-Layered Perovskite La1.5sr0.5coo4 Ceramics

Low‐Temperature Dielectric Relaxations Associated with Mixed‐Valent Structure in Na0.5Bi0.5Cu3Ti4O12

Relaxor-like behaviors in Na1/2Bi1/2Cu3Ti4O12 ceramics

Low-temperature relaxations associated with mixed-valent structure in Sr2 TiMnO6

Dielectric Relaxations in Pure, La-doped, and (la, Co)-codoped BiFeO3: Post-sintering Annealing Studies

Dielectric Relaxations of Laalo3 Ceramics over Broad Temperature Range

Temperature dependent conductivity, dielectric relaxation, electrical modulus and impedance spectroscopy of Ni substituted Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$

Dielectric Relaxation and Phase Transition at Cryogenic Temperatures in 0.65[Pb(Ni_1/3Nb_2/3)O_3]-0.35PbTiO_3 Ceramics

High‐Temperature Dielectric Relaxation in Pb(Mg1/3Nb2/3)O3–PbTiO3 Single Crystals