Abstract:Currently, low heat Portland (LHP) cement is widely used in mass concrete structures. The magnesia expansion agent (MgO) can be adopted to reduce the shrinkage of conventional Portland cement-based materials, but very few studies can be found that investigate the influence of MgO on the properties of LHP cement-based materials. In this study, the influences of two types of MgO on the hydration, as well as the shrinkage behavior of LHP cement-based materials, were studied via pore structural and fractal analysis. The results indicate: (1) The addition of reactive MgO (with a reactivity of 50 s and shortened as M50 thereafter) not only extends the induction stage of LHP cement by about 1–2 h, but also slightly increases the hydration heat. In contrast, the addition of weak reactive MgO (with a reactivity of 300 s and shortened as M300 thereafter) could not prolong the induction stage of LHP cement. (2) The addition of 4 wt.%–8 wt.% MgO (by weight of binder) lowers the mechanical property of LHP concrete. Higher dosages of MgO and stronger reactivity lead to a larger reduction in mechanical properties at all of the hydration times studied. M300 favors the strength improvement of LHP concrete at later ages. (3) M50 effectively compensates the shrinkage of LHP concrete at a much earlier time than M300, whereas M300 compensates the long-term shrinkage more effectively than M50. Thus, M300 with an optimal dosage of 8 wt.% is suggested to be applied in mass LHP concrete structures. (4) The addition of M50 obviously refines the pore structures of LHP concrete at 7 days, whereas M300 starts to refine the pore structure at around 60 days. At 360 days, the concretes containing M300 exhibits much finer pore structures than those containing M50. (5) Fractal dimension is closely correlated with the pore structure of LHP concrete. Both pore structure and fractal dimension exhibit weak (or no) correlations with shrinkage of LHP concrete.

Expansion Properties and Microstructure Characterization of Cement Paste Mixed with Reactive MgO

Hydration Characteristics and Expansive Mechanism of MgO Expansive Agents

Influence of MgO on the Hydration and Shrinkage Behavior of Low Heat Portland Cement-Based Materials via Pore Structural and Fractal Analysis

Effects of reactive MgO on durability and microstructure of cement-based materials: Considering carbonation and pH value

Enhanced Carbonation Curing of Cement Pastes with Dolomite Additive

The Influence of the Hydration Procedure of MgO Expansive Agent on the Expansive Behavior of Shrinkage-Compensating Mortar

Engineering Performance and Expansion Mechanism of MgO Expansion Agent in Ultra-High Performance Concrete (UHPC)

Cementitious and hardening properties of magnesia (MgO) under ambient curing conditions

Influence of fineness of MgO expansive agent on expansion, mechanical strength, and microstructure of fly ash-Portland cement paste

Influence of Chemical Activity and Curing Temperature on Expansion Properties of Magnesium Oxide Expansive Agents

Expansion Mechanism and Properties of Magnesium Oxide Expansive Hydraulic Cement for Engineering Applications

Effects of Different Reactive MgOs on the Hydration of MgO-Activated GGBS Paste

Effect of Different Reactive MgOs on the Hydration of MgO-activated Ground Granulated Blast Furnace Slag Paste

RESEARCH ON THE EXPANSI8VE MECHANISM OF MODERATE HEAT PORTLAND CEMENT WITH SLIGHT EXPANSION

Micro-Change Process of Calcium–Magnesium Double Expansive Agent and Its Performance Characterization in Cement-Based Materials

Strength and Drying Shrinkage of Reactive MgO Modified Alkali-Activated Slag Paste

Effects of Reactivity of MgO Expansive Agent on Its Performance in Cement-Based Materials and an Improvement of the Evaluating Method of MEA Reactivity

Influence of Lightly Burned MgO on the Mechanical Properties and Anticarbonization of Cement-Based Materials

Investigation of effects of reactive MgO on autogenous and drying shrinkage of near-neutral salt activated slag cement

EXPANSIVE PROPERTY AND PORE STRUCTURE CHARACTERISITICS OF MAGNESIUM OXIDE SLIGHT EXPANSIVE CEMENT- FLY ASH BINDING MATERIAL

Effect of MgO and gypsum content on long-term expansion of low heat Portland slag cement with slight expansion