Abstract:Admixture and water-cement ratio are important factors affecting the development of properties of cement mortar or concrete. In order to study the influence of admixtures and water-cement ratio on the hydration products and the mechanical properties of cement-based materials, the study combined hydration reaction mechanism of pure cement and silicate admixture, derived the formulae of hydration products, theoretical maximum mixing amount and total porosity of composite cement-based materials, and investigated the effects of mixing amount of cement mortar with fly ash, steel slag and lithium slag on total porosity, mechanical properties and hydration products. This paper designed 3 gradients of water-cement ratio (0.50, 0.42 and 0.34), 3 kinds of admixtures (lithium slag, fly ash and steel slag) and 2 contents (20% and 60%); the ratio of cementitious material to sand was 1:2.5, and then, molding specimen accorded with the mix of mortar in the triple mold and the mechanical properties of mortar were tested when specimen was cured to 1, 3, 7, 28 and 90 d. The results showed that, after the same content of fly ash, steel slag and lithium slag incorporation, the contents of hydration products of composite cementitious materials, i.e. calcium hydroxide (CH) and calcium silicate hydrate (CSH), and the total porosity were smaller than those of pure cement; when the water-cement ratio decreased from 0.50 to 0.34, the total porosity of cement mortar decreased from 16.0% to 9.3%, and the contents of CH and CSH increased for the compound cement-based materials with mixing amount of 5%, but the increments were not big; the porosity of fly ash, steel slag and lithium slag cement-based composite materials reduced from 16.6%, 17.2% and 16.0% to 9.9%, 10.9% and 9.3%, respectively. When the admixture amount increased to 10%, the variation of porosity and hydration products of the 3 kinds of mortar was different. The content of hydration products (CH and CSH) of composite cementitious materials was still smaller than that of pure cement. Compared to pure cement, the contents of CH and CSH of lithium slag mortar reduced by about 81.1% and 4.2%, fly ash mortar reduced by about 20.9% and 9.5%, and steel slag mortar reduced by approximately 3.0% and 9.5%, respectively. The porosity of lithium slag, fly ash and steel slag mortar increased by 0.1%, 3.6% and 7.6%, respectively. Among the 3 kinds of admixtures, the theoretical maximum mixing amount of fly ash was the maximum, followed by lithium slag, and the steel slag’s theoretical maximum mixing amount was the minimum. It was found that the compressive strength of lithium slag cement-based composite material was prior to fly ash and steel slag cement-based composite materials. In early stage (14 days ago), the compressive strength of fly ash mortar was prior to steel slag mortar; when water-cement ratio was relatively high, the compressive strength of steel slag mortar was close to fly ash. When the mixing amount was 20%, the compressive strength of lithium slag cement mortar was prior to pure cement mortar; if the mixing amount was 60%, the compressive strength of fly ash, steel slag and lithium slag mortar was worse than pure cement mortar. The study provides theoretical basis for material adding in mortar and concrete.

Influence of Inorganic Admixture on Performance of Sticky Rice-Lime Mortar and Its Mechanism

Influence of Admixtures on Properties of Traditional Sticky Rice-lime Mortar and Their Mechanisms

The Synergy Effect of Limestone Powder and Mineral Admixtures on the Mechanical Property of Mortar

Chemical And Microscopic Study Of Masonry Mortar In Ancient Pagodas In East China

Influence of prepared silicate on properties of traditional sticky rice-lime mortar

Synergistic Improvement Earthen Mortars with Tung Oil, Sticky Rice Pulp, and Aerial Lime: Application for the Conservation of Rammed Earth Structures Damaged by Exfoliation

Effect of waterproof agent on performance of inorganic lightweight aggregate thermal insulating mortar

Textual and Experimental Studies on The Compositions of Traditional Chinese Organic–Inorganic Mortars

Erosion of Aerial Lime and Sticky Rice Mortars by Cyclic Wetting–drying and Dilute Sulfate Acid Actions

An Experimental Study on Application of Sticky Rice–lime Mortar in Conservation of the Stone Tower in the Xiangji Temple

Influence of Anti-cracking Fiber on Properties of Traditional Sticky Rice-lime Mortar

Microstructural Insights into the Lime Mortars Mixed with Sticky Rice Sol–gel or Water: A Comparative Study

Influence of Sticky Rice and Jaggery Sugar Addition on Lime Mortar

Study on the shear properties of masonry pagoda mortar and its influencing factors

A case study and mechanism investigation of typical mortars used on ancient architecture in China

Study of Sticky Rice-Lime Mortar Technology for the Restoration of Historical Masonry Construction.

EXPERIMENTAL STUDY ON PHYSICAL AND MECHANICAL PROPERTIES OF STICKY RICE-LIME MORTAR

Stuay of Mineral Admixtures as Fine Aggregate on Hydration Products and Spectral Performance of Mortar

Traditional Mortar Represented by Sticky Rice Lime Mortar—one of the Great Inventions in Ancient China

Study on the Traditional Lime Mortar from the Memorial Archway in the Southern Anhui Province

Influence of admixture and water-cement ratio on hydration products and mechanical properties of cement-based materials