Abstract:SiO2@Au@TiO2 core-shell nanostructures with tunable decoration amount of Au nanoparticles have been successfully synthesized by combining three individual synthesis steps with calcination. The as-prepared samples were characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), N-2 adsorption-desorption, X-ray photoelectron emission spectroscopy (XPS), and UV-vis diffuse reflectance spectroscopy. The photocatalytic activities of the samples were evaluated by photocatalytic degradation of naproxen in aqueous solution under visible light irradiation. Results show that the as-obtained core-shell nanostructure is composed of a SiO2 core with an average diameter of similar to 337 nm, tunable content of Au nanoparticles adsorbed on the surface of SiO2 core, and an outer layer of TiO2 with an average thickness of similar to 7.0 nm. Photocatalysis experiments indicate that the SiO2@Au@TiO2 core-shell nanostructures with Au decoration amount of 0.1 wt% (denotes as SiAuTi-2) exhibit the highest photocatalytic activity since it has the suitable decoration amount of Au nanoparticles for harvesting the visible-light energy and for prohibiting the recombination of free excitons. For fast separation of the catalysts, superparamagnetic cores of Fe3O4 were embedded in the SiO2@Au@TiO2 core-shell nanostructures and hence they can be separated from aqueous solution by an external magnetic field within 10 min. (C) 2013 Elsevier B.V. All rights reserved.

Synthesis and Characterization of Cage-Like Core–shell Structured TiO2 Hollow Microspheres

Synthesis of TiO2 Hollow Spheres with Tunable Pore Structure and Enhanced Photocatalytic Activity

Hollow TiO 2 microspheres assembled with rutile mesocrystals: Low-temperature one-pot synthesis and the photocatalytic performance

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Synthesis and Characterization of N-Doped Hollow Tio2 Microspheres

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Simultaneous formation of silica-protected and N-doped TiO2 hollow spheres using organic–inorganic silica as self-removed templates

Mesoporous TiO2 Single-Crystal Polyhedron-Constructed Core–Shell Microspheres: Anisotropic Etching and Photovoltaic Property

Fabrication of mesoporous core-shell structured titania microspheres with hollow interiors.

Facile and large-scale synthesis of hollow TiO2 nanostructures from TiCl3 solution

Template-free Hydrothermal Preparation of Mesoporous TiO2 Microspheres on a Large Scale

Effect of Key Parameters on the Morphology Transformation of Three-Dimensional TiO2 Solid Microspheres

Hierarchical Nanosheet-Assembled Yolk–shell TiO2microspheres with Improved Photocatalytic Activity

A Novel Etching and Reconstruction Route to Ultrathin Porous TiO2 Hollow Spheres for Enhanced Photocatalytic Hydrogen Evolution

Hierarchical porous TiO2@C hollow microspheres: one-pot synthesis and enhanced visible-light photocatalysis

TiO2 Hollow Spheres Composed of Highly Crystalline Nanocrystals Exhibit Superior Lithium Storage Properties.

Large-Scale Fabrication Of Tio2 Hierarchical Hollow Spheres

Efficient fabrication and photocatalytic properties of TiO2 hollow spheres