Abstract:Aiming at enhancing the electrochemical characteristic of RE-Mg-based composite, the partial substituting La with Ce experiment in the composites was conducted, and the surface modification treatment of the alloys was performed by mechanical coating Ni. By means of mechanical trituration, The La 10-x Ce x Mg 80 Ni 5 (x = 0–2) + y wt% Ni (y = 50–200) compound materials which have the structures of nanocrystalline and amorphous were synthesized. In order to make sense of the principle action of Ce and Ni elements in structural and electrochemical properties of the material, some deep research were carried out. According to the final results, the as-milled composites have the electrochemical hydrogen absorption and hydrogen desorption abilities at room temperature. Having no use for activation, the as-milled composites can reach the maximum discharge capacities when the first cycling was carried out. With the Ni value x changed from 50 to 200, the discharge capacity was varied from 70.5 mAh/g to 902.1 mAh/g; moreover, the capacity retention rate at 20th cycle (S 20 ) and high rate dischargeability (HRD) of the (x = 0) composite were heightened from 67.2 % to 82.3 %, from 50.6 % to 55.7 % respectively. The composites' (y = 100) discharge capacity has a maximum value 118.5 mAh/g when the Ce value x is 1. The capacity retention rate (S 20 ) is enhanced from 53.3 % to 68.5 % by lifting Ce content from x = 0 to x = 2. what's more, the high-rate discharge ability (HRD), the electrochemical impedance spectrum (EIS), potentiodynamic polarization curves, and potential-step measurements all intimate that substituting La with Ce clearly promotes the composites' electrochemical kinetic properties, but maximum values emerge only when the x value is 1.

Influence of Substitution of La by Ce on the Glass Forming Ability and Crystallization Behavior of Al–Ni–La Alloys

Effects of Substitution of La by Other Rare-Earth Elements on the Glass Forming Ability of Al86ni9la5 Alloy

Influence of Mutual Substitution Between La and Gd on the Glass-Forming Ability of Al–Ni–La–Gd Alloys

Influence of Substitution of La by Gd on Crystallization Behavior of Al-Ni-La Metallic Glasses

Influence of Similar Atom Substitution on Glass Formation in (La-Ce)-Al-Co Bulk Metallic Glasses

Dependences of the Crystallization Behavior of Al–Ni–La Amorphous Alloys on La and Ni Contents

Glass Forming Ability of Al–Ni–La Alloys with Si Addition

Glass Forming Ability and Primary Crystallization Behavior of Al–Ni–Ce Alloys

The Effect Of Al Substitution For Ni On The Structure And Electrochemical Properties Of Ab(3)-Type La2mg(Ni1-Xalx)(9) (X=0-0.05) Alloys

Effects of La content on the glass transition and crystallization process of Al–Ni–La amorphous alloys

Effects of Replacing Ni by Co on the Crystallization Behaviors of Al–Ni–La Amorphous Alloys

Glass Forming Ability and Crystallization Behavior of Al–Ni–RE Metallic Glasses

Influence of the Substitution Ce for La on Structural and Electrochemical Characteristics of La0.75-xCexMg0.25Ni3Co0.5 (x=0, 0.05, 0.1, 0.15, 0.2 At. %) Hydrogen Storage Alloys

Effect of La-substitution on Microstructure and Magnetic Property of Melt-Spun (nd1−la )13fe81b6 Alloys

Effect of partial substitution of Ce for La on the structural, magnetic and abnormal thermal expansion properties of La1-Ce Fe11.2Al1.8 alloys

Effects of the partial substitutional alloying elements on the crystallization behavior of Mg65Cu25Gd10 metallic glass: Ag versus Ni

Influence of La on the atomic structure of Al Cu alloy liquid

Clarifying the alloying effects of La and Ce on the pitting corrosion behaviour of Al-based metallic glasses

Glass Formation Ability and Isothermal Crystallization of Melt-Spun NdNiCuAl Ribbons

Structure Alterations in Al-Y-Based Metallic Glasses with La and Ni Addition

Effect of Ce replacing La on the electrochemical performance of amorphous grain boundaries Mg-Ni-based materials