Magnetic Properties and Room-Temperature Magnetocaloric Effect in the Doped Antipervoskite Compounds Ga1−xAlxCMn3 (0≤X≤0.15)
B. S. Wang,C. C. Li,S. Lin,J. C. Lin,L. J. Li,P. Tong,W. J. Lu,X. B. Zhu,Z. R. Yang,W. H. Song,J. M. Dai,Y. P. Sun
DOI: https://doi.org/10.1016/j.jmmm.2011.02.046
IF: 3.097
2011-01-01
Journal of Magnetism and Magnetic Materials
Abstract:We report the effects of Al doping on the structure, magnetic properties, and magnetocaloric effect of antiperovskite compounds Ga1−xAlxCMn3 (0≤x≤0.15). Partial substitutions of Al for Ga enhance the Curie temperature (from 250K for x=0.0 to 312K for x=0.15) and the saturation magnetization. On increasing the doping level x, the maximum values of the magnetic entropy change (−ΔSM) decreases while the temperature span of −ΔSM vs. T plot broadens. Furthermore, the relative cooling power (RCP) is also studied. For 20kOe, the RCP value tends to saturate at a high doping level (for x=0.12, 119J/kg at 296K). However, at 45kOe, the RCP value increases quickly with increasing x (for x=0.15, 293J/kg at 312K). Considering the relatively large RCP and inexpensive raw materials, Ga1−xAlxCMn3 may be alternative candidates for room-temperature magnetic refrigeration.