Abstract:LaFe11.6Si1.4/16 wt%La70Co30 composites were fabricated by hot-pressing (HP) followed by thermal diffusion treatment in the temperature range of 923-1273 K. Significant microstructural and phase evolution occurred during diffusion heat treatment. Thermal decomposition (TD) occurred between 1023 and 1223 K, which increased the Curie temperature (T-C) but smeared out the magnetic transition, decreasing magnetic entropy change (-Delta S-M). Co atoms first diffused into the alpha-Fe(Si) and LaFeSi (1:1:1) phases. And then, the alpha-Fe(Co,Si) and La(Fe,Co)Si phases, attached to large LaFe11.6Si1.4 particles, transformed to a NaZn13-type La(Fe,Co,Si)(13) (1:13) phase at 1273 K. Hence, a core-shell La(Fe,Co,Si)(13) phase formed, resulting in a table-like magnetic entropy change over a wide temperature range (similar to 202-292 K). Greater Co diffusion and more homogeneity of the composition of the 1:13 phase could be achieved by increasing the annealing time. The maximum magnetic entropy change (-Delta S-M)(max) of the composites at 0-2 T could be increased from 5.62 J/(kg.K) at similar to 196 K to 8.81 J/(kg.K) at similar to 244 K. (C) 2020 Elsevier B.V. All rights reserved.

Superconductivity and Mechanical Properties for LaFe1-xZnxAsO0.85F0.15

Charge transfer and local structure distortion in Zn-doped LaFe 1−x Co x AsO

Charge redistribution and local lattice structure of (F, Zn)-codoped LaFeAsO superconductor

Synthesis and physical properties of $\rm\bf LaO_{1-x}F_xFeAs$

Effect of Zn doping on magnetic order and superconductivity in LaFeAsO

Superconductivity at 57.3 K in La-Doped Iron-Based Layered Compound Sm<sub>0.95</sub>La<sub>0.05</sub>O<sub>0.85</sub>F<sub>0.15</sub>FeAs

Superconductivity at 57.3 K in La-Doped Iron-Based Layered Compound Sm 0.95 La 0.05 O 0.85 F 0.15 FeAs

Superconductivity and critical current density in LaFeAsO1−xFx compounds

Superconductivity in (La<sub>1-x</sub>Ce<sub>x</sub>)(O<sub>0.9</sub>F<sub>0.1</sub>)FeAs and (La<sub>1-x</sub>Pb<sub>x</sub>)OFeAs

Superconductivity and Magnetic Properties in SmFe 1−x Co X AsO (x=0 to 1)

Short range magnetic order and effective suppression of superconductivity by manganese-doping in LaFe1-xMnxAsO1-yFy

Structural and superconducting properties of LaFeAs1−x Sb x O1−y F y

Enhanced Superconductivity of SmFeAsO Co-Doped by Scandium and Fluorine to Increase Chemical Inner Pressure

Superior Comprehensive Properties of LaFe 11.8 Si 1.2 /ce 60 Co 40 Magnetocaloric Composites

The synthesis of new FeAs-based superconductors

Magnetic and structural transitions in La$_{0.4}$Na$_{0.6}$Fe$_2$As$_2$ single crystals

Magnetic and Structural Transitions in La0.4Na0.6Fe2As2 Single Crystals

Density Functional Study of the Electronic Structure and Magnetism of LaFeAsO Alloyed with Zn

Microstructure, Phase Evolution and Magnetocaloric Properties of LaFe11.6Si1.4/La70Co30 Composite