Abstract:The effect of morphology of the long-period stacking ordered (LPSO) phase on mechanical properties of the Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (wt.%) alloy have been studied. The results reveal that the block-like 14H-LPSO phases in and near grain boundaries can be formed during heat treatment at high temperature, but low temperatures is conducive to form the needle-like 14H-LPSO phases within α-Mg grains. During heat treatment at fixed temperature for different time, the preferential nucleation sites of the 14H-LPSO phases are located in grain boundaries, then the14H-LPSO phases grow into the α-Mg matrix in the form of needle-like, the needle-like 14H-LPSO phases gradually decrease its length after growing a certain stage, at last the needle-like 14H-LPSO phases disappear completely. The decomposition of the block-like 14H-LPSO phases is found during furnace cooling after homogenization. After decomposition of the block-like 14H-LPSO phases, the rapid diffusion of Zn atoms into α-Mg matrix leads to form the needle-like 14H-LPSO phases within α-Mg matrix, but the retention of RE atoms in grain boundaries results in forming the Mg-RE particles. After extrusion and subsequent ageing, it is found that the alloy with the needle-like 14H-LPSO phases exhibit superior elongation than the alloy without the needle-like 14H-LPSO phase. The precipitates of peak-aged alloys are studied by TEM. The <112−0>α demonstrates that the stacking faults can be observed, the serious lattice distortion appears near the stacking fault. The [0001] zone axis shows that the β′ and a new rod phase are found, and the enrichment of RE atoms are detected in the two phase by HADDF-STEM. It seems to be that the rod phase can be subdivided into a plurality of mutually parallel structure unit.

Research on Long-Period-stacking-ordered Phase in Mg–Zn–Dy–Zr Alloy

The Effect of Morphology of the Long-Period Stacking Ordered Phase on Mechanical Properties of the Mg-7Gd-3Y-1Nd-1Zn-0.5Zr (wt.%) Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of the Morphology of Long-Period Stacking Ordered Phase on Mechanical Properties and Corrosion Behavior of Cast Mg-Zn-Y-Ti Alloy

On the Structure, Transformation and Deformation of Long-Period Stacking Ordered Phases in Mg-Y-Zn Alloys

Mechanical Properties of the Mg-Gd-Y-Zn-Zr Alloys with Different Morphologies of Long-Period Stacking Ordered Phases

Formation of long period stacking ordered phases in Mg-10Gd-1Zn-0.5Zr (wt.%) alloy

Effect of Heat Treatment on the Long-Period Stacking Ordered Phase and Mechanical Properties of the Mg-10Y-2Zn-0.5Zr Alloy

Effects of Heat Treatment on the Morphology of Long-Period Stacking Ordered Phase and the Corresponding Mechanical Properties of Mg–9Gd–xEr–1.6Zn–0.6Zr Magnesium Alloys

Effects of an LPSO Phase Induced by Zn Addition on the High-Temperature Properties of Mg-9Gd-2Nd-(1.5Zn)-0.5Zr Alloy

Effects of Zr and Mn Additions on Formation of LPSO Structure and Dynamic Recrystallization Behavior of Mg-15Gd-1Zn Alloy

Effect on Zn on Microstructures and Mechanical Properties of Mg–Gd–Y–Zn LPSO Alloys

Deformation Behavior of an Extruded Mg–Dy–Zn Alloy with Long Period Stacking Ordered Phase

Effect of morphology of long period stacking ordered phase on mechanical properties of Mg-10Gd-1Zn-0.5Zr magnesium alloy

Influence of the morphology of long-period stacking ordered phase on the mechanical properties of as-extruded Mg-5Zn-5Y-0.6Zr magnesium alloy

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Microstructures and Properties of As-Cast Mg;Zn;Y; and Mg;Zn;Y;Gd; Alloys with LPSO Phase

Effect of Long-Period Stacking Ordered Phase on Dynamic Recrystallization in Mg-Y-Zn-Zr Alloy Processed by Backward Extrusion

Formation Behavior of 14H Long Period Stacking Ordered Structure in Mg–Y–Zn Cast Alloys with Different Α-Mg Fractions

Microstructures and Mechanical Properties of Mg–10Gd–6Y–2Zn–0.6Zr(wt.%) Alloy

The Roles of Long Period Stacking Ordered Structure and Zn Solute in the Hot Deformation Behavior of Mg-Gd-Zn Alloys