Abstract:Very active 40%Ir–10%V–3%Mo/C and 40%Ir–10%V–10%Mo/C (in weight) catalysts, as novel, suitable anode electrode materials in polymer electrolyte membrane fuel cells (PEMFCs), have been synthesized by an ethylene glycol (EG) reduction method. The nanostructured catalysts have been characterized by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (TEM). Ir nanoparticles, after modification with V and further with Mo, show a narrow particle size distribution centered at 2 nm, and are uniformly dispersed on Vulcan XC-72 supports. Investigation of the catalytic activity by means of linear sweep voltammetry (LSV) employing a rotating disk electrode (RDE) has revealed that 40%Ir–10%V–10%Mo/C catalyst exhibited very high electrocatalytic activity toward the hydrogen oxidation reaction (HOR). About 77% higher current density was obtained for 40%Ir–10%V–10%Mo/C compared to that of 40 wt.% commercial carbon-supported platinum catalyst (Pt/C), and 282% higher current density compared to that of the pure 40 wt.% Ir/C at 0.1 V versus RHE. The performance of a membrane electrode assembly (MEA) prepared with the 40%Ir–10%V–10%Mo/C as the anode catalyst generated a maximum power density of 598.4 mW cm−2 at 70 °C, which is 26.4% higher than that of commercially available Pt/C under air/H2 testing condition. The ternary 40%Ir–10%V–10%Mo/C catalyst was also tested for 10 ppm CO tolerance, and the results showed that the 40%Ir–10%V–10%Mo/C has much better CO tolerance than commercial Pt/C catalyst. The mechanism of the ternary 40%Ir–10%V–10%Mo/C catalyst may be a bi-functional mechanism.

High Performance by Applying IrCo/C Nanoparticles As an Anode Catalyst for PEMFC

Carbon Supported Ir Nanoparticles Modified and Dealloyed with M (M = V, Co, Ni and Ti) As Anode Catalysts for Polymer Electrolyte Fuel Cells

Development of Composite Non-Platinum IrFe (1:16)/C Nanoparticle As Novel Anodic Catalyst in PEMFC

High PEMFC performance by applying Ir-V nanoparticles as a cathode catalyst

Kinetics and electrocatalytic activity of IrCo/C catalysts for oxygen reduction reaction in PEMFC

Synthesis of a highly active carbon-supported Ir–V/C catalyst for the hydrogen oxidation reaction in PEMFC

Carbon-supported Ir-Ti As a Novel Cathode Catalyst for PEFCs

Highly Active Carbon-Supported Pt Nanoparticles Modified and Dealloyed with Co for the Oxygen Reduction Reaction

New non-platinum Ir-V-Mo electro-catalyst, catalytic activity and CO tolerance in hydrogen oxidation reaction

New Ir-V-W Electro-Catalyst Exceeding Pt for the Anode of Fuel Cells

Carbon‐supported Pt‐Co Nanowires As a Novel Cathode Catalyst for Proton Exchange Membrane Fuel Cells

Efficient Synthesis of Pt–Co Nanowires As Cathode Catalysts for Proton Exchange Membrane Fuel Cells

Carbon-Supported IrM (M=V, Mn, Fe, Co, and Ni) Binary Alloys As Anode Catalysts for Polymer Electrolyte Fuel Cells

Highly Active and Durable Pt–Co Nanowire Networks Catalyst for the Oxygen Reduction Reaction in PEMFCs

Carbon-supported Ir–V nanoparticle as novel platinum-free anodic catalysts in proton exchange membrane fuel cell

CO-Tolerant PEMFC Anodes Enabled by Synergistic Catalysis between Iridium Single-Atom Sites and Nanoparticles

The Application of Ir–V/C Catalyst As a Durable Anode Catalyst for a 1.5kw Proton Exchange Membrane Fuel Cell Stack

Preparation and Application of Pt-Ni Catalysts Supported on Cobalt-Polypyrrole-Carbon for Fuel Cells

Irco Metal-Alloy As A Novel Anode Catalyst For Pefcs

Effect of Metal Particle Size and Nafion Content on Performance of MEA Using Ir-V/C As Anode Catalyst

Cobalt-doped IrRu Bifunctional Nanocrystals for Reversal-Tolerant Anodes in Proton-Exchange Membrane Fuel Cells