Abstract:We present a facile low-cost method to produce nitrogen-doped holey graphene (N-HGE) and its application to supercapacitors. A composite of N-HGE and activated carbon (AC) was used as the electrode active material in organic-electrolyte supercapacitors, and the performances were evaluated. Melamine was mixed into graphite oxide (GO) as the N source, and an ultra-rapid heating method was used to create numerous holes during the reduction process of GO. X-ray photoelectron spectra confirmed the successful doping with 2.9–4.5 at.% of nitrogen on all samples. Scanning electron micrographs and Raman spectra revealed that a higher heating rate resulted in more holes and defects on the reduced graphene sheets. An extra annealing step at 1000 °C for 1 h was carried out to further eliminate residual oxygen functional groups, which are undesirable in the organic electrolyte system. Compared to the low-heating-rate counterpart (N-GE-15), N-HGE boosted the specific capacity of the supercapacitor by 42 and 22% at current densities of 0.5 and 20 A/g, respectively. The effects of annealing time (0.5, 1, and 2 h) at 1000 °C were also studied. Longer annealing time resulted in higher capacitance values at all current densities due to the minimized oxygen content. Volumetric specific capacitances of 49 and 24 F/cm3 were achieved at current densities of 0.5 and 20 A/g, respectively. For the high-power-density operation at 31,000 W/kg (or 10,000 W/L), an energy density as high as 11 Wh/kg (or 3.5 Wh/L) was achieved. The results indicated that N-HGE not only improved the conductivity of the composite supercapacitors but also accelerated ion transport by way of shortened diffusion paths through the numerous holes all over the graphene sheets.

Hydrothermal Synthesis of Macroscopic Nitrogen-Doped Graphene Hydrogels for Ultrafast Supercapacitor

Synthesis of the Graphene/Nickel Oxide Composite and Its Electrochemical Performance for Supercapacitors

Sprinkling MnFe2O4 Quantum Dots on Nitrogen-Doped Graphene Sheets: the Formation Mechanism and Application for High-Performance Supercapacitor Electrodes

Facile and Tunable Synthesis of Nitrogen-Doped Graphene with Different Microstructures for High-Performance Supercapacitors

Facile Synthesis of Nitrogen/Sulfur Co-doped Three-Dimensional Holey Graphene Hydrogels for High Supercapacitive Performance

N/S co-doped three-dimensional graphene hydrogel for high performance supercapacitor

Nanocellulose/nitrogen and fluorine co-doped graphene composite hydrogels for high-performance supercapacitors

Facile preparation of nitrogen/sulfur co-doped and hierarchical porous graphene hydrogel for high-performance electrochemical capacitor

Crumpled Nitrogen‐Doped Graphene Nanosheets with Ultrahigh Pore Volume for High‐Performance Supercapacitor

Nitrogen-Superdoped 3D Graphene Networks for High-Performance Supercapacitors.

Influence of Aqueous Electrolytes on the Electrochemical Behaviors of Nitrogen-Doped Graphene Hydrogel Electrodes for Supercapacitors

Nitrogen‐Superdoped 3D Graphene Networks for High‐Performance Supercapacitors

Optimized Supercapacitive Performance of Graphene-Hydrogel by Porous Texture Controlling

Flash Nitrogen-Doped Graphene for High-Rate Supercapacitors

Three-dimensional N/S Co-doped holey graphene oxide based hydrogel electrodes for high performance supercapacitors

Study on the Application of Nitrogen-Doped Holey Graphene in Supercapacitors with Organic Electrolyte

Nitrogen Doped Carbons Derived From Graphene Aerogel Templated Triazine-Based Conjugated Microporous Polymers for High-Performance Supercapacitors.

Synthesis of Sandwich-Like Graphene@mesoporous Nitrogen-Doped Carbon Nanosheets for Application in High-Performance Supercapacitors

High Performance Supercapacitors Based on Highly Conductive Nitrogen-Doped Graphene Sheets

Graphene/single-walled Carbon Nanotube Hybrids and Applications in Supercapacitors

Wet-spun, porous, orientational graphene hydrogel films for high-performance supercapacitor electrodes.