Abstract:In this paper, the early fatigue damage evaluation of high strength steel was discussed. By using CH-3600 Gauss meter and three channel metal magnetic memory probe, the three components of MMM signal, including Bx, By and Bz signals, were collected, and a non-ferromagnetic three-dimensional platform was employed. Based on the high cycle fatigue test, the Bx, By and Bz signals, corresponding to different fatigue cycles, were collected. The results show that the lift-off of probe is important for the characteristic parameter of Bx, By and Bz signals (defining Bxave, Byave and Kz, respectively), as lift-off of probe increases, the characteristic parameter decreases fast and tends to be stable gradually. As fatigue cycle increases, the changes on Bxave, Byave and Kz are very similar, but compared with Byave, the Bxave and Kz change more smoothly and are more suitable for evaluating the early fatigue damage. As fatigue stress increases gradually, the values of Bxave-2 and Kz-2 increases linearly. At last, the experimental results are explained on the base of grain slip and magnetostriction effect, and the interaction of magnetic domain, dislocation and the internal stress is considered to be as the main reason for the change of Bxave and Kz.

Experimental Study of Early Fatigue Nonlinear Ultrasonic Detection in Magnesium Alloy

Detection of Fatigue Damage in Aluminum Alloy Structures Using Nonlinear Ultrasonic Modulation

Three Orthogonally Arranged Ultrasounds Modulate Solidification Microstructures and Mechanical Properties for AZ91 Magnesium Alloy

Study on Synchronous Measurement of Vibration Fatigue of Aluminum Alloy

Research on Nonlinear Ultrasonic Testing Technology on Fatigue Process of Metal Materials

Low-Cycle Fatigue Behavior of Magnesium Alloy AZ91

Early fatigue damage evaluation based on nonlinear Lamb wave third-harmonic phase velocity matching

Acoustic Emission Study of Fatigue Crack Propagation in Extruded AZ31 Magnesium Alloy

Thermographic Study of AZ31B Magnesium Alloy under Cyclic Loading: Temperature Evolution Analysis and Fatigue Limit Estimation

Simulation and Testing of a Non-Linear Ultrasonic System for Testing the Debonding of the Adhesive Layers of Magnesium Alloys.

Evaluation of plastic damage for metallic materials under tensile load using nonlinear longitudinal waves

A nonlinear ultrasonic nondestructive testing method for microdefects of medical magnesium alloy coatings

Experimental Investigation of Second-Harmonic Lamb Wave Generation in Additively Manufactured Aluminum

Investigation of uniaxial low-cycle fatigue failure behavior of hot-rolled AZ91 magnesium alloy

High-cycle fatigue damage evaluation based on hysteresis nonlinearity using ultrasonic guided waves

Study on the early fatigue damage evaluation of high strength steel by using three components of metal magnetic memory signal

Evaluation of the fatigue life in aluminum alloy welded joint by nonlinear ultrasonic testing

Fatigue Damage Development in Extruded Mg-3al-Zn Magnesium Alloy

Fatigue Limit Evaluation of AZ31B Magnesium Alloy Based on Temperature Distribution Analysis

Metamaterial Improved Nonlinear Ultrasonics for Fatigue Damage Detection

Study on the characteristics of magneto acoustic emission for mild steel fatigue