Ca(BH4)2–LiBH4–MgH2: a Novel Ternary Hydrogen Storage System with Superior Long-Term Cycling Performance

Mingxia Gao,Jian Gu,Hongge Pan,Yiliu Wang,Yongfeng Liu,Chu Liang,Zhengxiao Guo

DOI: https://doi.org/10.1039/c3ta12472j

IF: 11.9

2013-01-01

Journal of Materials Chemistry A

Abstract:A ternary hydrogen storage system, of superior cyclic stability and high capacity, was developed from a mixture of Ca(BH4)(2), LiBH4 and MgH2 in molar ratios of 1 : 2 : 2. Investigation on both non-isothermal and isothermal hydrogen desorption/absorption properties shows that the hydrogen desorption starts from 320 degrees C and completes at 370 degrees C under a heating rate of 2 degrees C min(-1), releasing ca. 8.1 wt% H-2. The finishing temperature of desorption is much lower and the capacity much higher than any of the two-hydride mixtures in the ternary system. In particular, hydrogenation of the ternary system initiates at an extremely low temperature of ca. 75 degrees C and the onset dehydrogenation temperature is significantly reduced by 90 degrees C after the initial dehydrogenation/hydrogenation cycle, which is ascribed to the formation of an active dual-cation hydride of CaMgH3.72 for dehydrogenation in the hydrogenation process. There is ca. 7.6 wt% H-2 absorbed at 350 degrees C and 90 bar H-2 for 18 h for the system post-dehydrogenated at 370 degrees C for 30 min, demonstrating a reversibility of over 94%. The capacity seems to fade mainly in the initial few cycles and stabilizes after further cycling. The reversibility is as high as 97% and a dehydrogenation capacity of ca. 6.2 wt% H2 at the 10th cycle. Favourable kinetics and thermodynamics of hydrogen desorption/absorption are achieved, which are responsible for the low completion temperature and the superior cycling performance. Mechanisms of the improved dehydrogenation/hydrogenation properties including the cyclic behaviour of the system are also proposed in relation to microstructural analyses.