Abstract:Successive mesophase transformation induced by an anionic surfactant such as sodium dioctyl sulfosuccinate (AOT) has been demonstrated to fabricate four kinds of large pore mesoporous silica materials in a triblock copolymer F127 surfactant assembly system. The transformation of the highly ordered mesostructures from face-centered cubic (space group Fm (3) over barm) to body-centered Im (3) over barm then towards two-dimensional (2-D) hexagonal p6m and eventually to cubic bicontinuous Ia (3) over bard symmetries has been achieved by tuning the amount of AOT and 1,3,5-trimethylbenzene (TMB). Characterization by small-angle X-ray scattering (SAXS), powder X-ray diffraction (XRD), transmission electron microscopy (TEM) and N-2 sorption isotherms reveals that all mesoporous silica structures have highly ordered regularity in large domains and possess high surface areas, large pore volumes and uniform pore sizes. The expansion of hydrophobic volume in the amphiphilic Pluronic F127 surfactant associated with AOT and TMB molecules in an acidic media is attributed to the observed mesophase transformation. A further swelling of the surfactant micelles can be achieved by adding TMB molecules into the mixed AOT and F127 surfactants system due to their synergistic solubility enhancement, which gives rise to a long-range ordered 2-D hexagonal mesoporous silica structure with very large cell parameter (a = 16.5 nm) and pore size (similar to 12 nm). The understanding of the blend-surfactant assembly mechanism will lead to a more rational approach for economical and large-scale production of mesoporous materials with controllable structures.

An Efficient Route to Rapidly Access Silica Materials with Differently Ordered Mesostructures Through Counteranion Exchange

Sio2-Template Synthesis of Mesoporous Mgf2 Highly Effective for Cl/F Exchange Reaction

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Synthesis and characterization of MCM-49/ZSM-35 composite zeolites in the hexamethyleneimine and cyclohexamine system

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

A Highly Ordered Mesoporous Aluminosilicate, CMI-10, with a Si/Al Ratio of One

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

A Facile Way to Synthesize Mesoporous Silica with Ia3d Cubic Symmetry

A Unique Transformation Route for Synthesis of Rodlike Hollow Mesoporous Silica Particles

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Oxoanions-Induced Rapid Synthesis of Highly Ordered Mesoporous Silica

A Facile Aqueous Route To Synthesize Highly Ordered Mesoporous Polymers And Carbon Frameworks With Ia(3)Over-Bard Bicontinuous Cubic Structure

Rapid Synthesis of Ordered Mesoporous Silica with the Aid of Heteropoly Acids

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

An Easy Route For The Synthesis Of Ordered Three-Dimensional Large-Pore Mesoporous Organosilicas With Im-3m Symmetry

Direct Synthesis of High Quality Cubic Ia3d Mesoporous Material under Organosilane Assisted

Control of morphology in synthesizing mesoporous silica

Anionic Surfactant Induced Mesophase Transformation to Synthesize Highly Ordered Large-Pore Mesoporous Silica Structures

Low-cost route for synthesis of mesoporous silica materials with high silanol groups and their application for Cu(II) removal

Sustainable synthesis of ordered mesoporous materials without additional solvents

Ordering improvement of mesoporous silica materials templated from semi-fluorinated nonionic surfactants by introduction of organic additives