Synthesis, Structures and Single-Molecule Magnet Behaviour of Octanuclear and Decanuclear Dysprosium Clusters Based on [Dy4(μ4-O)] Tetrahedral Subunits
Guo Penghu,Liao Xiaofen,Leng Jidong,Tong Mingliang
DOI: https://doi.org/10.6023/a12110865
2013-01-01
Acta Chimica Sinica
Abstract:Two novel [Dy4(μ4-O)] based dysprosium(III) clusters, namely, [Dy8(bpt)8(μ4-O)2(μ-OMe)8(μ1,1,3,3-N3)(μ1,3-N3)(N3)2]•11H2O•9MeOH (1) and [Dy10(bpt)6(μ4-O)4(μ3-OMe)4(μ-OMe)8(μ-OAc)2(OAc)2]•40H2O (2) (Hbpt=3,5-bis(pyridin2-yl)-1,2,4-trizole), are synthesized successfully. To obtain complex 1, a mixture of DyCl3 (0.1 mmol), 2,2'-Hbpt (0.1 mmol) and NaN3 (0.15 mmol) was sealed in a 25 mL vessel and then heated at 160 °C in methanol condition (8 mL) for 72 h. The reaction of Dy(OAc)3 (0.17 mmol) and 2,2'-Hbpt (0.1 mmol) under the same condition as complex 1 yielded complex 2. Single-crystal X-ray diffraction reveals that complex 1 consists of a pair of [Dy4(μ4-O)] tetrahedral units bridged by two azido groups in μ1,1,3,3 and μ1,3 modes as well as two bpt ligands, while complex 2 possesses four edge-sharing [Dy4(μ4-O)] tetrahedral units. Magnetic susceptibility of polycrystalline samples were carried out using a SQUID magnetometer in the temperature range 2~300 K at 500 Oe dc field. The χMT value are 107.8 cm•K•mol for complex 1 and 133.6 cm•K•mol for complex 2 at 300 K, which are close to the expected values. The maximum values of magnetization at 1.8 K are 40.81 Nβ and 51.62 Nβ for 1 and 2, slightly smaller than the expected saturation values. For further investigation of the dynamic behaviour, ac susceptibility measurements were undertaken under zero-dc field between 1~1500 Hz, they both show temperature dependence and have maximum values in the χM′′ vs v plots above 1.8 K, indicating the presence of slow relaxation of the magnetization. After linear fitting the first four points of ln(τ/s) vs 1/T plot, we get energy barrier Ueff=9.83(9) K, pre-exponential factor τ0=1.63(2)×10 s for 1, and Ueff=12.05(2) K, τ0=6.75(8)×10 s for 2 respectively. The bridging mode of azido in complex 1 is novel and complex 2 holds the record for highest nuclearity among the reported pure lanthanide single-molecule magnets (SMMs) under zero dc field.