In situ preparation of flower-like α-Ni(OH) 2 and NiO from nickel formate with excellent capacitive properties as electrode materials for supercapacitors
yangyang zhang,yun liu,yiping guo,yu xin yeow,huanan duan,hua li,hezhou liu
DOI: https://doi.org/10.1016/j.matchemphys.2014.11.050
IF: 4.778
2015-01-01
Materials Chemistry and Physics
Abstract:Flower-like precursor with coexisting nickel formate and α-Ni(OH)2 was synthesized via a template-free and cost effective hydrothermal method. It is found for the first time that the decomposition behavior of nickel formate in the presence of α-Ni(OH)2 is completely different from that of pure nickel formate. At a heating temperature of 210 °C, α-Ni(OH)2, which is originally inside the precursor, serving as crystal nucleus could induce nickel formate to transform into α-Ni(OH)2 instead of previously reported highly active metallic Ni. After elevating the heating temperature to 250 °C, single-phase NiO, which well inherited the flower-like morphology of the precursor, was obtained. Electrochemical properties of the precursor, α-Ni(OH)2 and NiO were investigated systematically to provide deep insight into their differences in supercapacitor applications. The precursor shows a relatively high specific capacitance of 923 F g−1 at 1 A g−1 but a poor capacitance retention of ∼50% after 600 cycles. Both the flower-like α-Ni(OH)2 and NiO electrodes exhibit excellent long cycling lives with capacitance retention of 89% and 86% after 1000 cycles, respectively. More importantly, the specific capacitance of α-Ni(OH)2 electrode, which is as large as 810.4 F g−1 at 1 A g−1, is very outstanding.