Functionalized graphene nanofiber-based low-cost composite membrane for vanadium redox flow battery applications
Harun Khan,Aiswarya Kesh,Kothandaraman Ramanujam,Akhila Kumar Sahu
DOI: https://doi.org/10.1007/s12039-024-02318-x
2024-12-01
Journal of Chemical Sciences
Abstract:Nafion has gained widespread recognition as the predominant membrane due to its good proton conductivity, robust chemical resistance, and commendable mechanical stability. However, due to its well-developed water channels, it has poor barrier properties toward vanadium ions. Herein, to reduce vanadium ions permeability across the membranes without compromising the proton conductivity, graphene nanofiber (Herringbone type, GNF-H) as a filler has been incorporated into the Nafion matrix to fabricate the composite membrane. The membranes were subjected to physiochemical characterization, vanadium ion permeability, electrochemical impedance spectroscopy, and galvanostatic charge-discharge at different current densities. Vanadium permeability has significantly reduced in the 0.75% and 1% GNF-H composite membranes. Composite membranes (0.5%, 0.75%, and 1% GNF-H) showed a capacity of ~18.2, ~18.9, and ~16.8 Ah L −1 at 100 mA cm −2 , respectively, whereas Nafion TM 117 exhibited only ~16.3 Ah L −1 capacity at the same current density. The peak power of the cells consisted of 0.5, 0.75, and 1% GNF-H composite membrane and Nafion TM 117 is ~538, ~507, ~465 and 388 mW cm −2 , respectively. The present study concludes that applying Nafion/GNF-H in the VRFB system can be a promising strategy to reduce the vanadium ion permeation, cost-cutting and improve the VRFB performance.
chemistry, multidisciplinary