Polyamide derived from 4,4′-thiobis(methylene)dibenzoyl chloride and aliphatic diamine: interfacial synthesis and characterization

Gang Zhang,Yan Zhang,Dong-sheng Li,Guang-shun Huang,Xiao-jun Wang,Jie Yang

DOI: https://doi.org/10.1007/s00289-012-0829-4

IF: 2.843

2012-01-01

Polymer Bulletin

Abstract:A series of processable semi-aromatic polyamides containing thioether and methylene units were synthesized through the reaction of 4,4 ′ -thiobis(methylene)dibenzoyl chloride and aliphatic diamine by the method of interfacial polycondensation. These polyamides had excellent thermal properties with glass transition temperatures ( T g ) of 104.3–130.6 °C, melting temperatures ( T m ) of 300.3–303.8 °C, and initial degradation temperatures ( T d ) of 405.2–410.3 °C. They had wider processing windows than traditional semi-aromatic polyamides (such as PA6T can not be processed by melting) and can be processed by melting method. They had better tensile strengths of 57.6–64.1 MPa, low-temperature mechanical properties, low water absorption of 0.19–0.27 %, low dielectric constants of 3.11–3.95 at 100 kHz, and better melt flowability properties of 232–60.7, 301.9–78.8, and 423.1–83.6 Pa s under a shear rate ranging from 20 to 1,170 s −1 , respectively. In addition, these polyamides showed good corrosion resistance, they did not dissolve in solvents such as NMP, DMSO, hydrochloric acid (6 mol/l), and solution of NaOH (1 mol/l) and so on.