Polyfluorene (PF) Single-Chain Conformation, Β Conformation, and Its Stability and Chain Aggregation by Side-Chain Length Change in the Solution Dynamic Process
Bin Liu,Tao Li,Hao Zhang,Tengning Ma,Jiaxuan Ren,Bo Liu,Jinyi Lin,Mengna Yu,Linghai Xie,Dan Lu
DOI: https://doi.org/10.1021/acs.jpcc.8b03504
2018-01-01
Abstract:The effects of alkyl side-chain length with different carbon atom number, called poly(9,9-=di-hexlyfluorene) (PF6), poly(9,9-diheptylfluorene) (PF7), poly(9,9-dioctylfluorene) (PF8), poly(9,9-dinonylfluorene) (PF9), and poly(9,9-didecylfluorene) (PF10), on the polyfluorene (PF) single-chain conformation, beta conformation, and its stability and chain aggregation in the solution dynamic process were systematically investigated by dynamic/static light scattering, UV-vis absorption spectra, photoluminescence spectra, and scanning electron microscopy. beta conformation was the low energy chain conformation, and its characteristic peak was at 437, 427, and 428 nm in the UV vis spectrum of PF8, PF9, and PF10, respectively. It was interestingly found that the shape parameters (R-g/R-h) (i.e., ratio of radius of gyration (R-g) and hydrodynamic radius (R-h)) of PF single chains in toluene solution showed an odd even property with the increase in side-chain length, which revealed that PF chains with even carbon atoms were more rigid than those with odd carbon atoms. The highest contents of beta conformation were all similar to 42% in PF8, PF9, and PF10 toluene/ethanol mixed solutions, but PF8 most easily formed the beta conformation, PF9 followed, and PF10 was last. It was first found that the beta-conformation formation and content were strongly connected to the chain packing density but not to aggregation size. High chain packing density was more advantageous to beta-conformation formation; it had been well proved by static fractal dimension (d(f)), reflecting the compactness of chain aggregation (i.e., chain packing density) and the chain self-similarity, and calculated by exponential law from SLS. Besides, it was also found that the beta-conformation content could be stabilized at the maximum value range (42%) in the high ethanol content (80%) and independent of the side-chain length even after placing for 21 days, whereas in lower ethanol content (30 and 40%), the beta-conformation content could also be stabilized in two different time stages. The conclusions are significant to understand deeply the solution dynamics process of film formation based on condensed matter physics of the conjugated polymer to control its condensed matter structure to achieve photoelectric devices with high carrier mobility, stability, and efficiency.