Formation and Confined Crystallization of Polyethylene Nanophases in Epoxy Thermosets

Chongyin Zhang,Lei Li,Sixun Zheng

DOI: https://doi.org/10.1021/ma4000682

IF: 5.5

2013-01-01

Macromolecules

Abstract:In this contribution, we reported the investigation of the formation and confined crystallization behavior of polyethylene nanophases in epoxy thermosets. The nanostructured epoxy thermosets were prepared by the use of a poly(epsilon-caprolactone)-block-polyethylene-block-poly(epsilon-caprolactone) (PCL-b-PE-b-PCL) triblock copolymer. The crystalline midblock (viz. PE) of the triblock copolymer was prepared from an alpha,omega-diacetoxy-terminated polycyclooctadiene with the molecular weight as high as M-n = 11,000, which was synthesized via the ring-opening metathesis polymerization (ROMP) of cyclooctadiene catalyzed by Grubbs second generation catalyst The formation of PE nanophases epoxy thermosets was evidenced with transmission electronic microscopy (TEM), small-angle X-ray scattering (SAXS) and dynamic mechanical thermal analysis (DMTA). It was found that in the nanostructured thermosets, the spherical nanophases of PE with the size of 20-30 nm in diameter were dispersed into the continuous epoxy matrices. Wide angle X-ray diffraction (XRD) showed that the formation of PE nanophases did not alter the structure of PE crystals. The investigations of isothermal and nonisothermal crystallization kinetics showed that the crystallization of PE in the nanostructured thermosets was in a confined manner and the confinement has been interpreted on the basis of nanoscaled space, interdomain connectivity, and the cross-linked structures of epoxy matrices.