Upconversion luminescence of NaYF4: Yb3+, Er 3+ for temperature sensing

Shaoshuai Zhou,Kaimo Deng,Xiantao Wei,Guicheng Jiang,Changkui DUAN,Yonghu CHEN,Min YIN

DOI: https://doi.org/10.1016/j.optcom.2012.11.005

IF: 2.4

2013-01-01

Optics Communications

Abstract:Rare earth doped luminescent materials are promising candidates for temperature sensing. In this paper, pure β-NaYF4:20%Yb3+, 2%Er3+ microprisms were synthesized by hydrothermal method. The temperature dependence of the fluorescence intensity ratio (FIR) of emission bands centered at 525nm and 545nm was measured in the temperature range of 160–300 K under excitation of a 980nm diode laser. The monotonous increase of FIR with temperature shows that this material can be used for temperature sensing. The dependence of the FIR on temperature is fitted with an exponential function and the effective energy difference obtained is 752cm−1, which gives further a temperature sensitivity of 1.20%K−1 at 300K. The FIR technique was then used to study the effect of heating caused by laser excitation under various powers.