Abstract:The addition of nanostructures to polymeric materials allows for a direct interaction between polymeric chains and nanometric structures, resulting in a synergistic process through the physical (electrostatic forces) and chemical properties (bond formation) of constituents for the modification of their properties and potential cutting-edge materials. This study explores a novel in situ synthesis method for PDMS-%SiO2 nanoparticle composites with varying crosslinking degrees (PDMS:TEOS of 15:1, 10:1, and 5:1); particle concentrations (5%, 10%, and 15%); and sol-gel catalysts (acidic and alkaline). This investigation delves into the distinct physical and chemical properties of silicon nanoparticles synthesized under acidic (SiO2-a) and alkaline (SiO2-b) conditions. A characterization through Raman, FT-IR, and XPS analyses confirms particle size and agglomeration differences between both the SiO2-a and SiO2-b particles. Similar chemical environments, with TEOS and ethanol by-products, were detected for both systems. The results on polymer composites elucidate the successful incorporation of SiO2 nanoparticles into the PDMS matrix without altering the PDMS's chemical structure. However, the presence of nanoparticles did affect the relative intensities of specific vibrational modes over composites from −35% to 24% (Raman) and from −14% to 59% (FT-IR). The XPS results validate the presence of Si, O, and C in all composites, with significant variations in atomic proportions (C/Si and O/Si) and Si and C component analyses through deconvolution techniques. This study demonstrates the successful in situ synthesis of PDMS-SiO2 composites with tunable properties by controlling the sol-gel and crosslinking synthesis parameters. The findings provide valuable insights into the in situ synthesis methods of polymeric composite materials and their potential integration with polymer nanocomposite processing techniques.

Preparation of PDMS/SiO2 Nanocomposites Via Ultrasonical Modification and Miniemulsion Polymerization

Preparation of PDMS/SiO_2 Nanocomposites Via Miniemulsion Polymerization

Preparation of nano-SiO2/polyacrylates composites via miniemulsion polymerization

Preparation of PDMS-ormosil and Its Application in Miniemulsion Polymerization

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

A Novel In Situ Sol-Gel Synthesis Method for PDMS Composites Reinforced with Silica Nanoparticles

Preparation and Characterization of PDMS Emulsion/Silica Gel Hybrid Water Dispersions

Preparation and characterization of polymer/silica nanocomposites via double in situ miniemulsion polymerization

Preparation of Solvent-borne Acrylic-based Polyurethane-Modified Silica Nanocomposites

Silica /polydicyclopentadiene nanocomposites: Preparation, characterization, and mechanical properties

Preparation of SiO2/PMMA Composite Particles Via Conventional Emulsion Polymerization

Synthesis of Silica/polystyrene Monocore-Shell Nanocomposite Particles Via Miniemulsion Polymerization

Synthesis of SiO2/Polystyrene Nanocomposite Particles Via Miniemulsion Polymerization

Reinforcement of Polydimethylsiloxane Through Formation of Inorganic–organic Hybrid Network

Preparation and Morphology of SiO 2 /PMMA Nanohybrids by Microemulsion Polymerization

Preparation of polymeric/inorganic nanocomposite particles in miniemulsions: II. Narrowly size-distributed polymer/SiO2 nanocomposite particles

Synthesis and Characterization of Polystyrene/Nanosilica Organic-Inorganic Hybrid

Fabrication of silica/PDMS hybrid nanoparticles by a novel solvent adjustment route.