Li+ incorporation and defects creation processes imposed by X-ray and UV irradiation in Li codoped Y3Al5O12:Ce scintillation crystals
S. Zazubovich,Valentyn V. Laguta,Maksym Buryi,Vladimir Babin,Pavel Machek,Karol Bartosiewicz,Shunsuke Kurosawa,Akihiro Yamaji,Akira Yoshikawa,Katerina Ulicna,Vojtech Chlan,Helena Stepankova,Martin Nikl
DOI: https://doi.org/10.1039/d2tc04520f
IF: 6.4
2022-12-20
Journal of Materials Chemistry C
Abstract:Cerium doped rare-earth aluminum garnets represent an important class of scintillation and luminescent materials widely used in different technical fields including the medical imaging and the solid state white light sources whose performance has to be further improved. One of the most effective tools in improving the light yield and timing characteristics of these materials is their codoping with optically inactive ions. Using electron paramagnetic resonance (EPR), 7Li nuclear magnetic resonance, and thermally stimulated luminescence (TSL), Li+ incorporation and defect formation processes imposed by X-ray and UV irradiation are studied in the Li+ codoped Y3Al5O12:Ce (YAG:Ce) garnet scintillation crystals. The EPR study shows that the Ce3+ content in the Li+ codoped crystals does not depend visibly on the Li concentration. The EPR spectra of X-ray irradiated Li+ codoped YAG crystals reveal the presence of both isolated O- centers (a hole trapped at the oxygen ion) and O- centers stabilized by the neighboring Li+ ion. The latter centers are responsible for the TSL peak at 320 K. Our data also show that at low Li concentration in the melt, the Li+ ions mainly substitute for Y3+ ions. However, at high Li+ ions concentration (1 at.% in melt), the Li+ ions substitute for Al3+ ions as well. Strong increase of oxygen vacancies concentration in the Li+ codoped crystals suggests that namely oxygen vacancies serve as effective compensators of the negative excess charge introduced into the crystal lattice by Li+ ions, suppressing thus the Ce3+ Ce4+ conversion process, which plays an important role in acceleration of the Ce3+ luminescence. The obtained data suggest that the decrease of a slow component in the scintillation decay of the Li+ ions codoped crystals is caused, at least partly, by redistribution of trapped charge carries to more thermally stable centers.
materials science, multidisciplinary,physics, applied